SABIC® LDPE PCG22
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® LDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | DKX3Mg_SABICLDPEPCG22.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Low density polyethylene for Healthcare Description SABIC® LDPE grades for healthcare applications are produced under controlled conditions resulting in high product quality, consistency and a high level of purity. SABIC® LDPE PCG22 is an additive free grade, typically designed for healthcare packaging and can typically be converted by Injection Molding to produce caps and closures. It exhibits a high MFR for good flow properties. Compliance to Regulations SABlC® LDPE PCG22 complies with the relevant monographs of the European Pharmacopoeia. The product mentioned herein may not be used for medical healthcare devices or materials intended for temporary or permanent implementation in the human body. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.919 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/2.16 kg | 22 | g/10 min | ISO 1133 |
| 190°C/5.0 kg | 75 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) | ISO 1133 | ||
| 190°C/2.16 kg | 29.0 | cm³/10min | ISO 1133 |
| 190°C/5.0 kg | 98.0 | cm³/10min | ISO 1133 |
| Environmental Stress-Cracking Resistance (60°C, 3.00 mm, Rhodacal-DS10, Compression Molded) | 3.00 | hr | Internal method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness 1(Shore D, Compression Molded) | 45 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 2(2.00 mm, Compression Molded) | 175 | MPa | ISO 527-2/1BA/50 |
| Tensile Stress 3 | ISO 527-2/1BA/50 | ||
| Yield, 2.00mm, molded | 8.00 | MPa | ISO 527-2/1BA/50 |
| Fracture, 2.00mm, molded | 7.00 | MPa | ISO 527-2/1BA/50 |
| Tensile Strain 4(Break, 2.00 mm, Compression Molded) | 400 | % | ISO 527-2/1BA/50 |
| Tensile Creep Modulus 5 | ISO 899-1 | ||
| 1 hr | 80.0 | MPa | ISO 899-1 |
| 1000 hr | 45.0 | MPa | ISO 899-1 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact 6 | ISO 180/A | ||
| -30°C, molded | 5.0 | kJ/m² | ISO 180/A |
| 23°C, molded | 42 | kJ/m² | ISO 180/A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 7(0.45 MPa, Unannealed) | 39.0 | °C | ISO 75-2/B |
| Vicat Softening Temperature 8 | 82.0 | °C | ISO 306/A |
| Melting Temperature (DSC) | 105 | °C | DIN 53765 |
| Enthalpy Change | 104 | J/g | DIN 53765 |
| Note Message | |
|---|---|
| 1 . | Compression moulding conditions of test specimen (according to ISO 293) : moulding temp: 160 °C, cooling rate: 40 °C/minConditioning of test specimen: temp. 23 °C, relative humidity 50 %, 24 hours |
| 2 . | Compression moulding conditions of test specimen (according to ISO 293) : moulding temp: 160 °C, cooling rate: 40 °C/minConditioning of test specimen: temp. 23 °C, relative humidity 50 %, 24 hours |
| 3 . | Compression moulding conditions of test specimen (according to ISO 293) : moulding temp: 160 °C, cooling rate: 40 °C/minConditioning of test specimen: temp. 23 °C, relative humidity 50 %, 24 hours |
| 4 . | Compression moulding conditions of test specimen (according to ISO 293) : moulding temp: 160 °C, cooling rate: 40 °C/minConditioning of test specimen: temp. 23 °C, relative humidity 50 %, 24 hours |
| 5 . | Test specimen according to ISO 3167, thickness 4 mmDetermined at 23 °C, 3 MPa |
| 6 . | Compression moulding conditions of test specimen (according to ISO 293) : moulding temp: 160 °C, cooling rate: 40 °C/minConditioning of test specimen: temp. 23 °C, relative humidity 50 %, 24 hours |
| 7 . | Compression moulding conditions of test specimen (according to ISO 293) : moulding temp: 160 °C, cooling rate: 40 °C/minConditioning of test specimen: temp. 23 °C, relative humidity 50 %, 24 hours |
| 8 . | Compression moulding conditions of test specimen (according to ISO 293) : moulding temp: 160 °C, cooling rate: 40 °C/minConditioning of test specimen: temp. 23 °C, relative humidity 50 %, 24 hours |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MAXAMID™ EPDM666G33-BK09 | Pier One Polymers, Inc. | Nylon 66/6 | MAXAMID™ |
| SABIC® PPcompound 108CS20 | Saudi Basic Industries Corporation (SABIC) | PP, Unspecified | SABIC® PPcompound |
| Flontech® FT-1-5 | Guarniflon S.p.A. - Flontech Division | PTFE | Flontech® |
| Generic SEPS | Generic | SEPS | Generic |
| Kynar® LBG | Arkema | PVDF | Kynar® |