Nymax™ GF1200 A30 FR BL286
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Nymax™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | DKFGTG_Nymax-GF1200-A30-FR-BL286.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Glass Fiber Reinforced PA66 Compound with Flame Retardant. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.64 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.30 - 0.40 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | 170 | MPa | ASTM D638 |
| Flexural Modulus 2 | 10000 | MPa | ASTM D790 |
| Flexural Strength 3 | 250 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm) | 80 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 240 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+12 | ohms | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | V-0 | Internal method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 90.0 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Rear Temperature | 260 - 280 | °C | |
| Middle Temperature | 260 - 280 | °C | |
| Front Temperature | 260 - 280 | °C | |
| Mold Temperature | 65.0 - 85.0 | °C |
| Injection instructions |
|---|
| Injection Pressure: MED-HIGHHold Pressure: MED-HIGHScrew Speed: MODERATEBack Pressure: LOW |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 1.3 mm/min |
| 3 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mirakutoran® TPU E 398 | Japan Mirakutoran Inc. | TPU Alloy | Mirakutoran® TPU |
| Sylvin 8250-60 Natural | Sylvin Technologies Incorporated | PVC, Flexible | Sylvin |
| Vistek 3013 | Visual Polymer Technologies, LLC | TP, Unspecified | Vistek |
| TOTAL Polypropylene Lumicene® M 3661 | TOTAL Refining & Chemicals | PP Homopolymer | TOTAL Polypropylene |
| APEX® 76-5066-H | Teknor Apex Company | PVC, Flexible | APEX® |