Order Products : sales@su-jiao.com
BJB Epoxy TC-1651 A/B
| Category: | Epoxy , Epoxy; Epoxide |
| Manufacturer: | BJB Enterprises, Inc. |
| Trademark: | BJB Epoxy |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | DGfgAg_BJB-Epoxy-TC-1651-A-B.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TC-1651 A/B is an aluminum powder filled epoxy casting resin system that provides service temperatures in the range of 340°F (171°C). TC-1651 A/B is most commonly used for the construction of molds that require good heat conductivity, outstanding durability, and that provide production run capability. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.70 | g/cm³ | ASTM D792 |
| Specific Gravity | |||
| Part A : 25°C | 1.796 | g/cm³ | |
| Part B : 25°C | 0.988 | g/cm³ | |
| Shrinkage | 0.20 | % | ASTM D2566 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Demold Time (25°C) | 16.0 to 24.0 | hr | |
| Gel Time | 3.0 | hr | ASTM D2471 |
| Work Time (25°C) 1 | 2.0 | hr |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brookfield Viscosity - Mixed (25°C) | 12.8 | Pa·s |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 90 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 55.8 | MPa | ASTM D638 |
| Flexural Modulus | 7310 | MPa | ASTM D790 |
| Flexural Strength | 73.1 | MPa | ASTM D790 |
| Compressive Strength | 190 | MPa | ASTM D695 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 113 | °C | ASTM D648 |
| CLTE - Flow | 3.6E-5 | cm/cm/°C | ASTM D3386 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Part A | Mix Ratio by Weight: 100 | ||
| Part B | Mix Ratio by Weight: 9.0 | ||
| Shelf Life | 52 | wk |
| Note Message | |
|---|---|
| 1 . | 1 lb mass |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sanren Y600 (1st-grade) | SINOPEC Shanghai Petrochemical Co. Ltd. | PP Homopolymer | Sanren |
| Abistir® 7120/V0-UV BIANCO 0154 | SO.F.TER. SPA | ABS | Abistir® |
| AKROMID® B3 GK 15 natural (1824) | AKRO-PLASTIC GmbH | Nylon 6 | AKROMID® |
| KumhoSunny PA/ABS HNB0225G2 | Shanghai KumhoSunny Plastics Co., Ltd. | ABS+Nylon | KumhoSunny PA/ABS |
| Kinta HI5603 | Kinta Technology (Hong Kong) Co., Ltd. | PC+ABS | Kinta |