E-RIALFILL H 15 40 T2
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | RIALTI Srl |
| Trademark: | E-RIALFILL |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | DGXtuU_E-RIALFILL-H-15-40-T2.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PP homopolymer obtained by meticulous recycling of industrial scraps, 40% talc filled High flowability for injection molding, excellent dimensional stability and high stiffness. Available only in the version in black color |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.25 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 14 | g/10 min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 0.95 | % | |
| Flow | 0.95 | % | |
| Water Absorption 1(23°C, 24 hr) | 0.030 | % | ISO 62 |
| Ash Content | 40 | % | ISO 3451 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Accelerated Oven Aging (150°C) | 6.3 | day | ISO 4577 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, 15 sec) | 76 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2/20 | ||
| Yield, 23°C | 28.0 | MPa | |
| Break, 23°C | 25.0 | MPa | |
| Tensile Strain | ISO 527-2/20 | ||
| Yield, 23°C | 3.0 | % | |
| Break, 23°C | 5.0 | % | |
| Flexural Modulus 2(23°C) | 4000 | MPa | ISO 178 |
| Flexural Stress (23°C) | 45.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength (23°C) | 17 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact Strength | ISO 180/1A | ||
| -20°C | 2.1 | kJ/m² | |
| 23°C | 2.5 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 120 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 75.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 152 | °C | ISO 306/A50 |
| -- | 95.0 | °C | ISO 306/B50 |
| Ball Pressure Test (125°C) | Pass | IEC 335 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 100 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 200 to 220 | °C | |
| Mold Temperature | 40.0 to 60.0 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | 50%RH |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC V964A | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| Veroplas SER20 | PlastxWorld Inc. | ABS | Veroplas |
| Yanshan PS 666D | SINOPEC Beijing Yanshan Petrochemical | PS (GPPS) | Yanshan PS |
| Geon™ Vinyl Flexible A90U2 | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| WELLAMID Nylon 6000 MRCF 15/15 HWCP | CP-Polymer-Technik GmbH & Co. KG | Nylon 6 | WELLAMID Nylon |