Edgetek™ CY4000 BK006
| Category: | PC+PBT , Polycarbonate + PBT |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Edgetek™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | DFObcx_Edgetek-CY4000-BK006.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Impact modified PC/PBT alloy with outstanding impact strength and chemical resistance |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.21 | g/cm³ | ASTM D792 |
| Molding Shrinkage (3.00 mm) | 0.40 - 0.70 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | 61.0 | MPa | ASTM D638 |
| Flexural Modulus 2 | 2300 | MPa | ASTM D790 |
| Flexural Strength 3 | 95.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm) | 650 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 100 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+15 | ohms | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | Internal method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 - 90.0 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Processing (Melt) Temp | 240 - 260 | °C | |
| Mold Temperature | 80.0 - 100 | °C |
| Injection instructions |
|---|
| Injection Pressure: MED-HIGHHold Pressure: MED-HIGHScrew Speed: MODERATEBack Pressure: LOW |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 1.3 mm/min |
| 3 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 2926-67LG Clear | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| VESTAMID® L X7293 | Evonik Industries AG | Nylon 12 | VESTAMID® L |
| ABSCOM® S106 | Polymer Compounders Limited | ABS | ABSCOM® |
| NYCOA Polyamide 1976 | Nycoa (Nylon Corporation of America) | Nylon 6 Alloy | NYCOA Polyamide |
| Cri-Line HFLT-615 | Cri-Tech, Inc. | Fluorelastomer | Cri-Line |