Ultramid® 8232G HS FR
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | BASF Corporation |
| Trademark: | Ultramid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | DFE45Q_Ultramid-8232G-HS-FR.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Ultramid 8232G HS FR is a 25% glass fiber reinforced, heat stabilized, flame retardant PA6 injection molding compound exhibiting excellent melt stability characteristics. It combines flame retardant ability with an excellent balance of high strength, stiffness and heat distortion temperature. Applications Ultramid 8232G HS FR is generally recommended for applications such as connectors, terminal blocks, switches and receptacles, coil bobbins, and appliance housings. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.62 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.30 | % | |
| Water Absorption | ASTM D570 | ||
| 24 hr | 0.90 | % | |
| Saturation | 4.0 | % | |
| Equilibrium, 50% RH | 1.1 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 121 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break, 23°C) | 157 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 3.0 | % | ASTM D638 |
| Flexural Modulus (23°C) | 8970 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 232 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 110 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 195 | °C | ASTM D648 |
| Peak Melting Temperature | 220 | °C | ASTM D3418 |
| RTI Elec | UL 746 | ||
| 0.840 mm | 130 | °C | |
| 1.50 mm | 130 | °C | |
| 2.50 mm | 130 | °C | |
| 3.00 mm | 130 | °C | |
| RTI Imp | UL 746 | ||
| 0.840 mm | 105 | °C | |
| 1.50 mm | 115 | °C | |
| 2.50 mm | 115 | °C | |
| 3.00 mm | 115 | °C | |
| RTI Str | UL 746 | ||
| 0.840 mm | 105 | °C | |
| 1.50 mm | 115 | °C | |
| 2.50 mm | 115 | °C | |
| 3.00 mm | 120 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity (1.50 mm) | > 1.0E+13 | ohms·cm | ASTM D257 |
| Dielectric Strength 1(1.50 mm) | 29 | kV/mm | ASTM D149 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.840 mm | V-0 | ||
| 1.50 mm | V-0 | ||
| 2.50 mm | V-0 5VA | ||
| 3.00 mm | V-0 5VA |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Processing (Melt) Temp | 250 to 290 | °C | |
| Mold Temperature | 80.0 to 95.0 | °C | |
| Injection Pressure | 3.50 to 12.5 | MPa | |
| Injection Rate | Fast |
| Note Message | |
|---|---|
| 1 . | Method A (Short-Time) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Wanthane® WHT-1180 | Wanhua Chemical Group Co., Ltd. | TPU-Polyester | Wanthane® |
| KetaSpire® KT-851 | Solvay Specialty Polymers | PEEK | KetaSpire® |
| Karina BLACK PVC COMPOUND 813-48/ 1-A-ERYB | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LNP™ THERMOCOMP™ DF006 compound | SABIC Innovative Plastics Asia Pacific | PC | LNP™ THERMOCOMP™ |
| 3M™ Dyneon™ Fluoroelastomer FC 1610N | 3M Advanced Materials Division | Fluorelastomer | 3M™ Dyneon™ Fluoroelastomer |