Marlex® 9398
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Chevron Phillips Chemical Company LLC |
| Trademark: | Marlex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | DDx0Xg_Marlex-9398.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Marlex® 9398 is a High Density Polyethylene material. It is available in Latin America or North America for extrusion or pipe extrusion. Important attributes of Marlex® 9398 are:
Typical application of Marlex® 9398: Electrical/Electronic Applications |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.945 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/21.6 kg) | 11 | g/10 min | ASTM D1238 |
| Environmental Stress-Cracking Resistance | |||
| 100% Igepal, Compression Molded, F50 | > 2000 | hr | ASTM D1693B |
| 100% Igepal, Compression Molded, F50 | > 2000 | hr | ASTM D1693C |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, Compression Molded) | 22.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, Compression Molded) | 800 | % | ASTM D638 |
| Flexural Modulus - 2% Secant 3(Compression Molded) | 900 | MPa | ASTM D790 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -75.0 | °C | ASTM D746A |
| Note Message | |
|---|---|
| 1 . | Type IV, 51 mm/min |
| 2 . | Type IV, 51 mm/min |
| 3 . | 13 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TOTAL Polypropylene PPR 3221 | TOTAL Refining & Chemicals | PP Random Copolymer | TOTAL Polypropylene |
| Niblan V100 | Soredi S.p.a. | PBT | Niblan |
| Next Nylon 66 Prime Series PXH-01NC | Next Polymers Ltd. | Nylon 66 | Next Nylon 66 Prime Series |
| PLUSTEK PA112NT | Polyram Ram-On Industries | Nylon 66 | PLUSTEK |
| POLYFORT® FPP 22 T K1093 | A. Schulman Europe | PP Homopolymer | POLYFORT® |