Jamplast JPPPO20GF
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | Jamplast, Inc. |
| Trademark: | Jamplast |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | DDklH2_Jamplast-JPPPO20GF.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| JPPPO20. 20% Glass reinforced. FDA compliance (restrictions apply). Low water absorption. Hydrolitic stability. Dimensional stability. Suitable for fluid engineering applications including pump housings and impellers, valve components and others. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/5.0 kg) | 9.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.20 to 0.50 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.060 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (L-Scale) | 106 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 6200 | MPa | ASTM D638 |
| Tensile Strength 2(Break) | 90.3 | MPa | ASTM D638 |
| Tensile Elongation 3(Break) | 2.6 | % | ASTM D638 |
| Flexural Modulus 4(50.0 mm Span) | 5800 | MPa | ASTM D790 |
| Flexural Strength 5(Yield, 50.0 mm Span) | 160 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -40°C | 96 | J/m | |
| 23°C | 120 | J/m | |
| Unnotched Izod Impact (23°C) | 650 | J/m | ASTM D256 |
| Instrumented Dart Impact (23°C, Total Energy) | 22.6 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.20 mm | 141 | °C | |
| 0.45 MPa, Unannealed, 6.40 mm | 143 | °C | |
| 1.8 MPa, Unannealed, 3.20 mm | 135 | °C | |
| 1.8 MPa, Unannealed, 6.40 mm | 138 | °C | |
| CLTE | ASTM E831 | ||
| Flow : -40 to 40°C | 2.9E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 8.3E-5 | cm/cm/°C | |
| RTI Elec | 90.0 | °C | UL 746 |
| RTI Imp | 90.0 | °C | UL 746 |
| RTI Str | 90.0 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength (3.20 mm, in Oil) | 17 | kV/mm | ASTM D149 |
| Dielectric Constant | ASTM D150 | ||
| 50 Hz | 2.86 | ||
| 60 Hz | 2.86 | ||
| Dissipation Factor | ASTM D150 | ||
| 50 Hz | 8.0E-4 | ||
| 60 Hz | 8.0E-4 | ||
| Arc Resistance 6 | PLC 7 | ASTM D495 | |
| High Amp Arc Ignition (HAI) | PLC 4 | UL 746 | |
| High Voltage Arc Tracking Rate (HVTR) | PLC 4 | UL 746 | |
| Hot-wire Ignition (HWI) | PLC 4 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.47 mm) | HB | UL 94 | |
| Oxygen Index | 26 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 to 121 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 30 to 70 | % | |
| Rear Temperature | 266 to 316 | °C | |
| Middle Temperature | 277 to 321 | °C | |
| Front Temperature | 288 to 327 | °C | |
| Nozzle Temperature | 299 to 327 | °C | |
| Processing (Melt) Temp | 299 to 327 | °C | |
| Mold Temperature | 82.2 to 110 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 20 to 100 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.1 mm/min |
| 2 . | Type I, 5.1 mm/min |
| 3 . | Type I, 5.1 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 1.3 mm/min |
| 6 . | Tungsten Electrode |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Delta HDPE 6510 | Delta Polymers | HDPE | Delta |
| DESLOY™ DSC892D | DESCO Co., Ltd. | PC+ABS | DESLOY™ |
| Elastron® G G400.A12.B | Elastron USA, Inc. | SEBS | Elastron® G |
| IDI BMC Rosite 3550F | IDI Composites International | TS, Unspecified | IDI BMC |
| PALPROP® R H 15 GF 20 | pal plast GmbH | PP Homopolymer | PALPROP® |