Generic ABS+Nylon - Glass Fiber
| Category: | ABS+Nylon , Acrylonitrile Butadiene Styrene + Nylon |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | DDBaPX_Generic-ABS-Nylon---Glass-Fiber.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic ABS+Nylon - Glass Fiber This information is provided for comparative purposes only. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.10 - 1.53 | g/cm³ | ASTM D792 |
| 23°C | 1.12 - 1.20 | g/cm³ | ISO 1183 |
| Molding Shrinkage | |||
| Flow : 23°C | 0.30 - 0.50 | % | ASTM D955 |
| 23°C | 0.25 - 0.80 | % | ISO 294-4 |
| Water Absorption (23°C, 24 hr) | 0.70 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (23°C) | 116 - 118 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2500 - 5400 | MPa | ISO 527-2 |
| Tensile Stress | |||
| Yield, 23°C | 43.0 - 56.4 | MPa | ISO 527-2 |
| Fracture, 23°C | 51.0 - 124 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 3.8 - 4.0 | % | ASTM D638 |
| Flexural Modulus | |||
| 23°C | 2140 - 8320 | MPa | ASTM D790 |
| 23°C | 2550 - 6500 | MPa | ISO 178 |
| Flexural Strength | |||
| 23°C | 75.8 - 207 | MPa | ASTM D790 |
| 23°C | 60.0 - 167 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 7.9 - 12 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 29 - 50 | kJ/m² | ISO 179 |
| Notched Izod Impact (23°C) | 80 - 160 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 107 - 202 | °C | ASTM D648 |
| Vicat Softening Temperature | 108 - 182 | °C | ISO 306 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 79.6 - 105 | °C | |
| Drying Time | 1.0 - 3.5 | hr | |
| Processing (Melt) Temp | 250 - 260 | °C | |
| Mold Temperature | 59.5 - 80.0 | °C |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic ABS+Nylon - Glass FiberThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| METALCAP PPC380Z82 | Polyram Ram-On Industries | PP Copolymer | METALCAP |
| Anjacom® 055/80-GF20 Black 91220 | Almaak International GmbH | PC+ABS | Anjacom® |
| Cariflex® IR0307 K | Kraton Polymers LLC | IR | Cariflex® |
| StarPrene® 6101-87 | Star Thermoplastic Alloys & Rubbers, Inc. | TPE | StarPrene® |
| Sylvin 8773-60D Brown 7361 | Sylvin Technologies Incorporated | PVC, Rigid | Sylvin |