PP ABS HI112H
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Performance Plastics, Ltd. |
| Trademark: | PP ABS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | DBvEUt_PP-ABS-HI112H.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| HI121H ABS: High Impact Grade; Suitable for Plating |
| General Information | |
|---|---|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 200°C/5.0 kg | 2.3 | g/10 min | |
| 220°C/10.0 kg | 23 | g/10 min | |
| 230°C/3.8 kg | 6.0 | g/10 min | |
| Molding Shrinkage - Flow | 0.40 to 0.70 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 111 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 22600 | MPa | ASTM D638 |
| Tensile Strength 2(Yield) | 51.3 | MPa | ASTM D638 |
| Tensile Elongation 3 | ASTM D638 | ||
| Yield | > 5.0 | % | |
| Break | > 10 | % | |
| Flexural Modulus 4 | 26000 | MPa | ASTM D790 |
| Flexural Strength 5 | 76.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Unnotched Izod Impact | ASTM D256 | ||
| -30°C, 3.20 mm | 78 | J/m | |
| -30°C, 6.40 mm | 78 | J/m | |
| 23°C, 3.20 mm | 230 | J/m | |
| 23°C, 6.40 mm | 230 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 6.40 mm | 90.0 | °C | |
| 0.45 MPa, Annealed, 6.40 mm | 93.0 | °C | |
| 1.8 MPa, Unannealed, 6.40 mm | 88.0 | °C | |
| 1.8 MPa, Annealed, 6.40 mm | 92.0 | °C | |
| Vicat Softening Temperature | 94.0 | °C | ASTM D1525 6 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Arc Resistance | PLC 6 | ASTM D495 | |
| Comparative Tracking Index (CTI) | PLC 0 | UL 746 | |
| High Amp Arc Ignition (HAI) | PLC 1 | UL 746 | |
| High Voltage Arc Tracking Rate (HVTR) | PLC 2 | UL 746 | |
| Hot-wire Ignition (HWI) | PLC 3 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | HB | ||
| 3.20 mm | HB | ||
| Flammability (3.20 mm) | FH3-34 | mm/min | IEC 707 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | 15 mm/min |
| 5 . | 15 mm/min |
| 6 . | Rate A (50°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NEOFLON™ EP-541 | DAIKIN AMERICA, INC. | ETFE | NEOFLON™ |
| ALTECH® PBT A 1000/100 | ALBIS PLASTIC GmbH | PBT | ALTECH® PBT |
| Ferro PP LPP40BK09BK | Ferro Corporation | PP, Unspecified | Ferro PP |
| Karina BROWN PVC COMPOUND -E MICRO-EX 6536/212 | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Sylvin 9067-80 Yellow 4147 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |