CRYSTALADD® HM-664

Category:	HDPE , High Density Polyethylene
Manufacturer:	Ravago Manufacturing Americas, LLC
Trademark:	CRYSTALADD®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	DBdGoO_CRYSTALADD-HM-664.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
NUCLEATOR MASTERBATCH HM-664 is an additive concentrate containing Milliken's Hyperform® HPN-210M nucleator. This masterbatch compound is designed to reduce cycle time in injection molded polyethylene parts, improve stiffness and HDT, and reduce or improve warpage challenges during processing. Key Features: Designed to be added to injection molded polyethylene parts Improved stiffness, HDT and part uniformity Uniform concentration of additives in concentrate form. Masterbatch pellet form for ease of addition and feeding into extrusion equipment Directions for Use: HM-664 is added to HDPE or LLDPE at 2.5% to 5% to achieve faster cooling, higher crystallization temperature and a higher crystallization rate. Parts are ejected from the mold with at a higher overall temperature but will have more completed crystal formation, allowing for a reduced overall cycle time. Note: Effectiveness is significantly reduced in LDPE due to the high long chain branching of the polymer. LDPE with MI > 25 can present some of the above performance improvements. FDA Compliance: This product is not approved for use in food contact applications at this time, but will be updated once regulatory tests are completed.

Message

NUCLEATOR MASTERBATCH

HM-664 is an additive concentrate containing Milliken's Hyperform® HPN-210M nucleator. This masterbatch compound is designed to reduce cycle time in injection molded polyethylene parts, improve stiffness and HDT, and reduce or improve warpage challenges during processing.

Key Features:

Designed to be added to injection molded polyethylene parts

Improved stiffness, HDT and part uniformity

Uniform concentration of additives in concentrate form.

Masterbatch pellet form for ease of addition and feeding into extrusion equipment

Directions for Use:

HM-664 is added to HDPE or LLDPE at 2.5% to 5% to achieve faster cooling, higher crystallization temperature and a higher crystallization rate. Parts are ejected from the mold with at a higher overall temperature but will have more completed crystal formation, allowing for a reduced overall cycle time.

Note: Effectiveness is significantly reduced in LDPE due to the high long chain branching of the polymer. LDPE with MI > 25 can present some of the above performance improvements.

FDA Compliance:

This product is not approved for use in food contact applications at this time, but will be updated once regulatory tests are completed.

General Information
Uses	Masterbatch
Forms	Pellets
Processing Method	Blow Molding Extrusion Film Extrusion Injection Molding

Physical	Nominal Value	Unit	Test Method
Density	0.950	g/cm³	ASTM D792
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)	8.2	g/10 min	ASTM D1238

Additional Information	Nominal Value	Unit	Test Method
Nucleating Agent - HPN-210M	4.0	%	Internal Method
Polymer Base	HDPE

Resin Grade	Manufacturer	Category	Trademark
Rilsan® BESNO P20 TL	Arkema	Nylon 11	Rilsan®
Shin-Etsu Elastomer KEG-2001-70A/B	Shin-Etsu Silicones of America	Silicone Rubber, HTV	Shin-Etsu Elastomer
THERMOLAST® V TV6LVN (Series: LTP)	KRAIBURG TPE	SEPS	THERMOLAST® V
Polifor® 5020/V2-EP NATURALE	SO.F.TER. SPA	PP Copolymer	Polifor®
EPAMOULD 295A14W	Epaflex Polyurethanes S.R.L.	TPU-Polyester	EPAMOULD