Borealis PP BB213CF
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | Borealis AG |
| Trademark: | Borealis PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | DBYyma_Borealis-PP-BB213CF.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
BB213CF is a heterophasic copolymer. This grade is suitable for the manufacturing of unoriented films on cast and tubular quench film lines. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 1.2 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus (23°C, Injection Molded) | 1100 | MPa | ISO 178 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 50 | µm | |
| Tensile Modulus | ISO 527-3 | ||
| MD : 50 µm | 670 | MPa | |
| TD : 50 µm | 610 | MPa | |
| Tensile Strength | ISO 527-3 | ||
| MD : 50 µm | 35.0 | MPa | |
| TD : 50 µm | 65.0 | MPa | |
| Tensile Elongation | ISO 527-3 | ||
| MD : Break, 50 µm | 700 | % | |
| TD : Break, 50 µm | 780 | % | |
| Instrumented Dart Impact (50 µm, Total Energy) | 26.0 | J | ISO 7765-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20°C | 2.5 | kJ/m² | |
| 23°C | 30 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature | 166 | °C | ISO 11357-3 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (50.0 µm) | 27 | ASTM D2457 | |
| Haze (50.0 µm) | 12 | % | ASTM D1003 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRIMALENE WPP831PR | Southern Polymer, Inc. | HDPE, HMW | PRIMALENE |
| ProTherm® 4526 | Axiall Corporation | CPVC | ProTherm® |
| Moplen HP561X | PolyMirae | PP, Unspecified | Moplen |
| WPP PP UP4I203 - Natural | Washington Penn Plastic Co. Inc. | PP Homopolymer | WPP PP |
| LACTEL® 25:75 DL-PLCL | DURECT Corporation | PCL | LACTEL® |