KetaSpire® KT-880P
| Category: | PEEK , Polyetheretherketone |
| Manufacturer: | Solvay Specialty Polymers |
| Trademark: | KetaSpire® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | DBUuwH_KetaSpire-KT-880P.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
KetaSpire® KT-880P is a high flow grade of unreinforced polyetheretherketone (PEEK) supplied in a natural-color coarse powder form. KetaSpire® PEEK is produced to the highest industry standards and is characterized by a distinct combination of properties, which include excellent wear resistance, best-in-class fatigue resistance, ease of melt processing, high purity and excellent chemical resistance to organics, acids and bases. These properties make it well-suited for applications in healthcare, transportation, electronics, chemical processing and other industrial uses. KetaSpire® KT-880P is intended for extrusion compounding. This powder is also available as KT-880NT in a natural-color pellet form for injection molding. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.30 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (400°C/2.16 kg) | 36 | g/10 min | ASTM D1238 |
| Water Absorption (24 hr) | 0.10 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3800 | MPa | ASTM D638 |
| Tensile Strength | 100 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield | 5.2 | % | |
| Break 1 | 10 to 20 | % | |
| Break 2 | > 60 | % | |
| Flexural Modulus | 3900 | MPa | ASTM D790 |
| Flexural Strength | 152 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 43 | J/m | ASTM D256 |
| Unnotched Izod Impact | No Break | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 159 | °C | ASTM D648 |
| Glass Transition Temperature | 147 | °C | ASTM D3417 |
| Melting Temperature | 343 | °C | ASTM D3417 |
| CLTE - Flow (-50 to 50°C) | 5.0E-5 | cm/cm/°C | ASTM E831 |
| Note Message | |
|---|---|
| 1 . | Crystallized |
| 2 . | Quenched |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mold Max® Stroke | Smooth-On, Inc | Silicone | Mold Max® |
| SCLAIR® FP020-D | NOVA Chemicals | LLDPE | SCLAIR® |
| Silmar® SIL93BE-1586 | Interplastic Corporation | Polyester, TS | Silmar® |
| Kingfa PC-WT01 | Kingfa | PC Alloy | Kingfa |
| HiFill® PA6/6 GF14 IM HS L | Techmer Engineered Solutions | Nylon 66 | HiFill® |