ALTECH® NXT PP-H A 2040/458 GF40 CP
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | ALBIS PLASTIC GmbH |
| Trademark: | ALTECH® NXT PP-H |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | DApZ9w_ALTECH-NXT-PP-H-A-2040-458-GF40-CP.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ALTECH® NXT PP-H A 2040/458 GF40 CP is a Polypropylene Homopolymer (PP Homopolymer) product filled with 40% glass fiber. It is available in Asia Pacific, Europe, or North America. Typical application: Automotive. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.21 | g/cm³ | ISO 1183 |
| Spiral Flow | |||
| -- 1 | 20.0 | cm | |
| -- 2 | 55.0 | cm | |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow : 24 hr | 0.50 to 0.70 | % | |
| Flow : 24 hr | 0.30 to 0.40 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 8350 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 100 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 3.0 | % | ISO 527-2 |
| Flexural Modulus | 7400 | MPa | ISO 178 |
| Flexural Stress | 135 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -- | 10 | kJ/m² | |
| -40°C | 5.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -- | 50 | kJ/m² | |
| -40°C | 30 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 150 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 135 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 3.0 | hr | |
| Processing (Melt) Temp | 200 to 270 | °C | |
| Mold Temperature | 20.0 to 90.0 | °C |
| Note Message | |
|---|---|
| 1 . | 1 mm |
| 2 . | 2 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Reslen PPH 40K | Polimarky Spolka Jawna | PP Homopolymer | Reslen |
| Trexprene® A67CW | Mitsubishi Chemical Performance Polymers, Inc. | TPV | Trexprene® |
| 4PROP® 9D12430 UV | 4Plas | PP Homopolymer | 4PROP® |
| Fainplast PVC CKL 64/K | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| LUBAN™ 1125 N | Oman Oil Refineries & Petroleum Indistries Co. (Orpic) | PP Homopolymer | LUBAN™ |