Braskem PP H357-09RSB
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Braskem Europe GmbH |
| Trademark: | Braskem PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | DANtDI_Braskem-PP-H357-09RSB.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Braskem H357-09RSB Polypropylene Resin is a homopolymer suited for high output, fast running cast film lines. Braskem H357-09RSB Polypropylene Resin has optimized rheology for fast extrusion capability and allows for easy film winding and cutting performance, as well as good printability after corona treatment. Films based on Braskem H357-09RSB Polypropylene Resin exhibit excellent optical properties, notably transparency and gloss. Braskem H357-09RSB Polypropylene Resin contains slip and antiblocking additives. Braskem H357-09RSB Polypropylene Resin is well suited for the production of transparent films with a thickness range of 15-150 microns. Applications for Braskem H357-09RSB Polypropylene Resin
Regulatory Information Braskem H357-09RSB Polypropylene Resin should comply with:
|
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.900 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 9.5 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield, Injection Molded) | 32.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield, Injection Molded) | 13 | % | ISO 527-2 |
| Flexural Modulus (Injection Molded) | 1200 | MPa | ISO 178 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 50 | µm | |
| Tensile Modulus | ISO 527-3 | ||
| 1% Secant, MD : 50 µm, Cast Film | 650 | MPa | |
| 1% Secant, TD : 50 µm, Cast Film | 650 | MPa | |
| Tensile Stress | ISO 527-3 | ||
| MD : Break, 50 µm, Cast Film | 38.0 | MPa | |
| TD : Break, 50 µm, Cast Film | 32.0 | MPa | |
| Tensile Elongation | ISO 527-3 | ||
| MD : Break, 50 µm, Cast Film | 500 | % | |
| TD : Break, 50 µm, Cast Film | 610 | % | |
| Dart Drop Impact (50 µm, Cast Film) | 220 | g | ISO 7765-1 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C, Injection Molded) | 5.0 | kJ/m² | ISO 179/1eA |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 1(0.45 MPa, Unannealed) | 110 | °C | ISO 75-2/B |
| Vicat Softening Temperature 2 | 151 | °C | ISO 306/A |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 50.0 µm, Cast Film) | 80 | ASTM D2457 | |
| Haze (50.0 µm, Cast Film) | 2.0 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | Injection Molded |
| 2 . | Injection Molded |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 281 TFE 15 | RTP Company | Nylon 66 | RTP |
| TOTAL Polyethylene D3720 | TOTAL Refining & Chemicals | MDPE | TOTAL Polyethylene |
| Tritan™ TX1000 | Eastman Chemical Company | Copolyester | Tritan™ |
| Elastron® V P.V101.A65.B | Elastron USA, Inc. | TPV | Elastron® V |
| LUVOCOM® 65-9048/L | LEHVOSS Group | PP Copolymer | LUVOCOM® |