HANWHA LDPE 5310
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | Hanwha Chemical |
| Trademark: | HANWHA LDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | DAIiMr_HANWHA-LDPE-5310.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| HANWHA LDPE 5310 is manufactured by ICI autoclave high pressure process and designed for variety of film application such as agriculture film and shrink film. LDPE 5310 has well balanced property of mechanical property and processability. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.923 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.80 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 13.7 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 700 | % | ASTM D638 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 50 | µm | |
| Tensile Strength | ASTM D882 | ||
| MD : Break, 50 µm | 25.5 | MPa | ASTM D882 |
| TD : Break, 50 µm | 21.6 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 50 µm | 400 | % | ASTM D882 |
| TD : Break, 50 µm | 600 | % | ASTM D882 |
| Dart Drop Impact (50 µm) | 95 | g | ASTM D1709 |
| Tensile Tear Strength | ASTM D1004 | ||
| MD : 50.0 µm | 98.1 | kN/m | ASTM D1004 |
| TD : 50.0 µm | 93.2 | kN/m | ASTM D1004 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -76.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 92.0 | °C | ASTM D1525 |
| Melting Temperature | 111 | °C |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Haze (50.0 µm) | 11 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 140 - 180 | °C |
| Extrusion instructions |
|---|
| Blow-up Ratio: 2 to 3Optimum Gage Range: 0.05 to 0.15 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Chiao Fu PA66 MD212G53 NAT | Chiao Fu Enterprises Co., Ltd. | Nylon 66 | Chiao Fu PA66 |
| ESENTTIA 01C25 | Polipropileno del Caribe S.A. | PP Impact Copolymer | ESENTTIA |
| Hostacom D M2 T32 | LyondellBasell Industries | PP Copolymer | Hostacom |
| IROGRAN® A 85 E 4993 FCM | Huntsman Corporation | TPU-Polyester | IROGRAN® |
| POLYfill PP EIP12030RF | Polykemi AB | PP+EPDM | POLYfill |