Fainplast EVA 807I
| Category: | EVA , Ethylene Vinyl Acetate Copolymer |
| Manufacturer: | Fainplast Compounds S.r.l |
| Trademark: | Fainplast |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | D9pP2o_Fainplast-EVA-807I.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Crosslinkable and expandable compound based on EVA. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.180 - 0.240 | g/cm³ | ISO 1183 |
| Molding Shrinkage (70°C, 24 hours) | < 2.0 | % | Internal method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | |||
| Shaw C | 57 - 63 | ASTM D2240 | |
| Shaw A, 381mm | 37 - 43 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break) | > 3.00 | MPa | ISO 527-2 |
| Tensile Strain (Break) | > 280 | % | ISO 527-2 |
| Abrasion Resistance | mm³ | Internal method |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Linear Thermal Expansion | 1.6 | % | Internal method |
| Injection instructions |
|---|
| Processing: This compound should be injected into moulds thermoregulated at 180-190 °C, where the crosslinking occurs in about 6/7 minutes. Upon opening the mould, the piece expands and its volume, depending on the type of material, increases with respect to the volume of the figure of the mould. Volume expansion is uniform in the three dimensions and increases linearly with a ratio of 1.6. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TOTAL Polyethylene XSene® HDPE XS 10H | TOTAL Refining & Chemicals | HDPE | TOTAL Polyethylene |
| VECTRA® E540i | Celanese Corporation | LCP | VECTRA® |
| DOWLEX™ 2344 | The Dow Chemical Company | PE Copolymer | DOWLEX™ |
| Kaneka MUH BM5600 | Kaneka Corporation | ABS | Kaneka MUH |
| Sumikon® FM-CF101 | SBHPP | Nylon, Unspecified | Sumikon® |