ALCOM® PC 740/4 UV CC1320-08LG
| Category: | PC , Polycarbonate |
| Manufacturer: | ALBIS PLASTIC GmbH |
| Trademark: | ALCOM® PC |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | D8cIKF_ALCOM-PC-740-4-UV-CC1320-08LG.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ALCOM® PC 740/4 UV CC1320-08LG is a Polycarbonate (PC) product filled with filler. It is available in Asia Pacific, Europe, or North America. Applications of ALCOM® PC 740/4 UV CC1320-08LG include automotive and lighting applications. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.20 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (300°C/1.2 kg) | 20.0 | cm³/10min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2400 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | ||
| Yield | 66.0 | MPa | |
| -- | 66.0 | MPa | |
| Tensile Strain | ISO 527-2 | ||
| Yield | 6.0 | % | |
| Break | 70 | % | |
| Flexural Modulus | 2450 | MPa | ISO 178 |
| Flexural Stress | ISO 178 | ||
| -- | 100 | MPa | |
| 3.5% Strain | 76.0 | MPa | |
| Flexural Strain at Flexural Strength | 7.0 | % | ISO 178 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Fire Performance (1.00 mm) | passed | FMVSS |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Half Power Angle - T(Y) 1 | |||
| 2.00 mm | 8.00 | ° | |
| 3.00 mm | 10.0 | ° | |
| 4.00 mm | 11.0 | ° |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -- | 12 | kJ/m² | |
| -40°C | 12 | kJ/m² | |
| -20°C | 12 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -- | No Break | ||
| -40°C | No Break | ||
| -20°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 124 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 142 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 | |
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 1.00 mm | 850 | °C | |
| 2.00 mm | 850 | °C | |
| 3.00 mm | 850 | °C | |
| 4.00 mm | 850 | °C |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance 2 | ISO 13468 | ||
| Total, 2000 µm | 88.7 | % | |
| Total, 3000 µm | 88.5 | % | |
| Total, 4000 µm | 88.0 | % | |
| Haze | ISO 13468 | ||
| 2000 µm 3 | 92 | % | |
| 3000 µm 4 | 92 | % | |
| 4000 µm 5 | 93 | % |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| Circulation Dryer | 100 to 120 | °C | |
| Desiccant Dryer | 100 to 120 | °C | |
| Drying Time | |||
| Circulation Dryer | 4.0 to 12 | hr | |
| Desiccant Dryer | 2.0 to 3.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Processing (Melt) Temp | 270 to 310 | °C | |
| Mold Temperature | 80.0 to 100 | °C |
| Note Message | |
|---|---|
| 1 . | A, 2° |
| 2 . | A, 2° |
| 3 . | A, 2° |
| 4 . | A, 2° |
| 5 . | Ill. A, 2° |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SPI 962 BK | Service Polymers, Inc. | Nylon 66 | SPI |
| Jiangsu Sinarise EX9024X | Jiangsu Sinarise New Material Technology Co., Ltd | TPE | Jiangsu Sinarise |
| Karina COKE PVC COMPOUND 830-21/9-IS-RG | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Petro Rabigh PE FS250B | Rabigh Refining & Petrochemical Co. | LLDPE | Petro Rabigh PE |
| Sylvin 7011EE-82FU Brown 7246 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |