SCHULADUR® A3 GF 30 LM
| Category: | PBT+ASA , Polybutylene Terephthalate + ASA |
| Manufacturer: | A. Schulman Europe |
| Trademark: | SCHULADUR® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | D8LOLK_SCHULADUR-A3-GF-30-LM.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 30% glass fibre reinforced lasermarkable PBT/ASA-blend with high surface quality and reduced warpage |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.43 | g/cm³ | ISO 1183/A |
| Melt Volume-Flow Rate (MVR) (250°C/5.0 kg) | 20.0 | cm³/10min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 9500 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Break) | 115 | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Break) | 2.0 | % | ISO 527-2/1A/5 |
| Flexural Modulus 1 | 10500 | MPa | ISO 178 |
| Flexural Stress 2(2.5% strain) | 205 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 7.0 | kJ/m² | ISO 179/1eA |
| 23°C | 7.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 48 | kJ/m² | ISO 179/1eU |
| 23°C | 50 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 215 | °C | ISO 75-2/Bf |
| 1.8 MPa, not annealed | 175 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 210 | °C | ISO 306/A50 |
| -- | 140 | °C | ISO 306/B50 |
| Additional Information |
|---|
| 1.) Not for use in food contact applications2.) Not for use in medical or pharmaceutical applications |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Suggested Max Regrind | 10 | % | |
| Hopper Temperature | 70.0 | °C | |
| Rear Temperature | 230 | °C | |
| Middle Temperature | 245 | °C | |
| Front Temperature | 260 | °C | |
| Nozzle Temperature | 260 | °C | |
| Processing (Melt) Temp | 250 - 260 | °C | |
| Mold Temperature | 60.0 - 90.0 | °C | |
| Injection Pressure | 80.0 - 120 | MPa | |
| Injection Rate | Moderate-Fast | ||
| Holding Pressure | 40.0 - 70.0 | MPa | |
| Back Pressure | 5.00 - 10.0 | MPa | |
| Cushion | 2.00 - 5.00 | mm | |
| Vent Depth | 0.020 | mm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 8331-72FUV Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| LONGLITE® PBT 3030-200XR | CCP Group | PBT | LONGLITE® PBT |
| Pearlthane® ECO 12T95 | Lubrizol Advanced Materials, Inc. | TPU, Unspecified | Pearlthane® ECO |
| RTP 1099 X 136862 | RTP Company | PBT | RTP |
| Sarlink® TPE ML-1140DN NAT (PRELIMINARY DATA) | Teknor Apex Company | TPE | Sarlink® TPE |