Petrotene® PP A3 G24 T8 NTLA010 PH345
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Petropol Industry and Trade of Polymers LTDA |
| Trademark: | Petrotene® PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | D7zSDD_Petrotene-PP-A3-G24-T8-NTLA010-PH345.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Petrotene® PP A3 G24 T8 NTLA010 PH345 is a Polypropylene material filled with 24% glass fiber and 8.0% talc. It is available in Asia Pacific, Europe, Latin America, or North America for injection molding. Important attributes of Petrotene® PP A3 G24 T8 NTLA010 PH345 are:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.13 to 1.15 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 4.0 to 8.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.90 to 1.1 | % | ASTM D955 |
| Water Absorption (Equilibrium) | 1.0 to 2.0 | % | ASTM D570 |
| Ash Content | 30 to 34 | % | ASTM D2584 |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Operating Temperature | 90 | °C |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | 44.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 5.0 | % | ASTM D638 |
| Flexural Modulus | 3500 | MPa | ASTM D790 |
| Flexural Strength | 91.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 50 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 65.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 120 | °C | ASTM D1525 3 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+14 | ohms·cm | ASTM D257 |
| Dielectric Strength | 40 | kV/mm | ASTM D149 |
| Dissipation Factor (1 kHz) | 2.0E-3 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 190 to 230 | °C | |
| Mold Temperature | 40.0 to 50.0 | °C |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | Rate A (50°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC V972 NAT601 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| Polytron® P30B11 | Polyram Ram-On Industries | PP Homopolymer | Polytron® |
| RR Advantage PC 1812 Clear | Resin Resource, Inc. | PC | RR Advantage |
| Fainplast PVC ART 0699 | Fainplast Compounds S.r.l | PVC, Rigid | Fainplast PVC |
| En Chuan 336T | En Chuan Chemical Industries Co,. Ltd. | PS (GPPS) | En Chuan |