Elastollan® C60AW
| Category: | TPU-Polyester , Thermoplastic Polyurethane Elastomer (Polyester) |
| Manufacturer: | BASF Corp. Thermoplastic Polyurethanes |
| Trademark: | Elastollan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | D6vssR_Elastollan-C60AW.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Elastollan® C60AW is a polyester-based thermoplastic polyurethane (TPU) containing a plasticizer. It exhibits excellent abrasion resistance and toughness, good hydrolytic stability, good heat, oil, fuel and solvent resistance. It has excellent damping characteristics and outstanding resistance to tear propagation. Elastollan® C60AW is supplied uncolored in pellet form. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.14 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/3.8 kg) | 20 to 60 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 61 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (Injection Molded) | 5.52 | MPa | ASTM D412 |
| Flexural Modulus (Injection Molded) | 8.96 | MPa | ASTM D790 |
| Taber Abrasion Resistance | 40.0 | mg | ASTM D1044 |
| Abrasion - DIN | 20 | mm³ | DIN 53516 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Softening Point - DMA | 109 | °C | Internal Method |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412 | ||
| 100% Strain | 3.65 | MPa | |
| 300% Strain | 8.96 | MPa | |
| Tensile Strength | 23.4 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 760 | % | ASTM D412 |
| Tear Strength 1 | 64.8 | kN/m | ASTM D624 |
| Compression Set | ASTM D395B | ||
| 23°C, 22 hr | 20 | % | |
| 70°C, 22 hr | 45 | % |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | -52.0 | °C | Internal Method |
| Vicat Softening Temperature | 66.0 | °C | ASTM D1525 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Suggested Max Moisture | 0.030 | % | |
| Rear Temperature | 170 to 210 | °C | |
| Middle Temperature | 170 to 210 | °C | |
| Front Temperature | 170 to 210 | °C | |
| Nozzle Temperature | 200 to 210 | °C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 140 to 175 | °C | |
| Cylinder Zone 3 Temp. | 140 to 175 | °C | |
| Cylinder Zone 5 Temp. | 140 to 175 | °C | |
| Adapter Temperature | 160 to 175 | °C | |
| Die Temperature | 165 to 170 | °C |
| Note Message | |
|---|---|
| 1 . | Die C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TECHNYL® C 402 M NATURAL | Solvay Engineering Plastics | Nylon 6 | TECHNYL® C |
| ASTAMID™ MA3EG8 | Marplex Australia Pty. Ltd. | Nylon 66 | ASTAMID™ |
| Hyflon® PFA P125 | Solvay Specialty Polymers | PFA | Hyflon® PFA |
| Karina CLEAR PVC COMPOUND 80/221-IS-RG | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Sylvin 83033-75 Grey 9491 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |