Pearlthane® 11H94
| Category: | TPU-Capro , Thermoplastic Polyurethane Elastomer (Polycaprolactone) |
| Manufacturer: | Lubrizol Advanced Materials, Inc. |
| Trademark: | Pearlthane® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | D6nSQr_Pearlthane-11H94.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Pearlthane® 11H94 is a high performance polycaprolactone copolyester based TPU, supplied in form of translucent, colourless pellets, featuring adequate hardness as well as excellent flow and mechanical properties, including an outstandingly low compression set value. Product recommended for injection-moulding applications with an extremely short cycle time. Pearlthane® 11H94 is especially recommended for injection moulding applications such as: seals and gaskets, automotive parts and a variety of high performance technical parts. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.18 | g/cm³ | ASTM D792 |
| 20°C | 1.18 | g/cm³ | ISO 2781 |
| Moisture Content | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Abrasion Loss | 35.0 | mm³ | ISO 4649 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 95 | ASTM D2240, ISO 868 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412, ISO 527 | ||
| 100% strain | 12.0 | MPa | ASTM D412, ISO 527 |
| 300% strain | 23.0 | MPa | ASTM D412, ISO 527 |
| Tensile Strength (Yield) | 42.0 | MPa | ASTM D412, ISO 527 |
| Tensile Elongation (Break) | 520 | % | ASTM D412, ISO 527 |
| Tear Strength | |||
| -- 1 | 135 | kN/m | ASTM D624 |
| -- | 140 | kN/m | ISO 34-1 |
| Compression Set | ASTM D395B | ||
| 70°C, 22 hr | 32 | % | ASTM D395B |
| 70°C, 70 hr | 37 | % | ASTM D395B |
| 100°C, 22 hr | 43 | % | ASTM D395B |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature 2 | -39.0 | °C | ISO 11357-2 |
| Melting Temperature 3 | 197 - 207 | °C | Internal method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 - 110 | °C | |
| Drying Time | 2.0 | hr | |
| Rear Temperature | 210 | °C | |
| Middle Temperature | 215 | °C | |
| Front Temperature | 215 | °C | |
| Nozzle Temperature | 225 | °C | |
| Mold Temperature | 40.0 | °C |
| Injection instructions |
|---|
| Closing Force: 30 tonsScrew Diameter: 30 mmMaximum Hydraulic Pressure: 210 barMold: Plaque 120x120x2 mmL/D ratio: : 23 |
| Note Message | |
|---|---|
| 1 . | C mould |
| 2 . | 10°C /min |
| 3 . | Temperature at which MFI = 10 g/10 min @ 21.6 kg |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP VLF 84009 | RTP Company | PPA | RTP |
| alphalon™ E 40 T | Grupa Azoty ATT Polymers GmbH | Nylon 6 | alphalon™ |
| Karina GRAY PVC COMPOUND 651D18/408-B-IS-SD-BZ | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| PLUSTEK RA307G4 | Polyram Ram-On Industries | Nylon 66 | PLUSTEK |
| DAI-EL™ G-7201 | DAIKIN AMERICA, INC. | Fluorelastomer | DAI-EL™ |