LNP™ THERMOTUF™ IX02582 compound
| Category: | Nylon 612 , Polyamide 612 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOTUF™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | D5uDK8_LNP-THERMOTUF-IX02582-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOTUF IX02582 is a compound based on Nylon 6/12 resin containing Proprietary Filler(s). Added features of this material include: High Impact. Also known as: LNP* THERMOTUF* Compound PDX-I-02582 Product reorder name: IX02582 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.41 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.10 to 0.30 | % | |
| Across Flow : 24 hr | 1.0 to 3.0 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.16 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.28 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 12100 | MPa | ASTM D638 |
| -- | 11800 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break 2 | 156 | MPa | ASTM D638 |
| Break | 157 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Break 3 | 2.8 | % | ASTM D638 |
| Break | 2.8 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 4 | 9700 | MPa | ASTM D790 |
| -- 5 | 9980 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 233 | MPa | ISO 178 |
| Yield, 50.0 mm Span 6 | 233 | MPa | ASTM D790 |
| Break, 50.0 mm Span 7 | 235 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 160 | J/m | ASTM D256 |
| 23°C 8 | 16 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 1000 | J/m | ASTM D4812 |
| 23°C 9 | 62 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 20.0 | J | ASTM D3763 |
| -- | 5.10 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 214 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 10 | 210 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 198 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 11 | 196 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 3.9E-5 | cm/cm/°C | |
| Transverse : -30 to 30°C | 7.5E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.12 to 0.20 | % | |
| Rear Temperature | 254 to 266 | °C | |
| Middle Temperature | 260 to 271 | °C | |
| Front Temperature | 271 to 282 | °C | |
| Processing (Melt) Temp | 271 to 277 | °C | |
| Mold Temperature | 65.6 to 93.3 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 1.3 mm/min |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 mm |
| 11 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 9972-80 Grey 9466 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Braskem PP H 201 | Braskem | PP Homopolymer | Braskem PP |
| Delta HIPS 208 | Delta Polymers | PS (HIPS) | Delta |
| LNP™ STAT-KON™ DE003E compound | SABIC Innovative Plastics Europe | PC | LNP™ STAT-KON™ |
| Plaslube® POM HO TL15 | Techmer Engineered Solutions | Acetal (POM) Homopolymer | Plaslube® |