NYCOA Polyamide 5113 HS
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Nycoa (Nylon Corporation of America) |
| Trademark: | NYCOA Polyamide |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | D5Vdmo_NYCOA-Polyamide-5113-HS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
NYCOA 5113 HS is a 13% glass fiber reinforced, heat stabilized, impact modified Nylon 66 resin used for injection molding. NYCOA 5113 HS has been specifically formulated for improved ductility and impact strength vs standard grades of glass filled Nylon 66. Typical applications include shoe sole plates, hardware items and automotive under the hood applications. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.22 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.70 | % | ASTM D955 |
| Transverse flow | 1.2 | % | ASTM D955 |
| Water Absorption (24 hr) | 1.3 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 118 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 4620 | MPa | ASTM D638 |
| Tensile Strength 2 | 101 | MPa | ASTM D638 |
| Tensile Elongation 3(Break) | 4.0 | % | ASTM D638 |
| Flexural Modulus 4 | 3580 | MPa | ASTM D790 |
| Flexural Strength 5 | 140 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (6.35 mm) | 160 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 249 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 232 | °C | ASTM D648 |
| Melting Temperature | 258 | °C | DSC |
| Additional Information |
|---|
| The value listed as Melting Point DSC, was tested in accordance with ASTM D789. |
| Note Message | |
|---|---|
| 1 . | 51 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | 50 mm/min |
| 5 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Santoprene™ 8201-80 | ExxonMobil Chemical | TPV | Santoprene™ |
| Spartech Polycom SC2F-1090 | Spartech Polycom | PS (HIPS) | Spartech |
| ALTECH® PP-H A 2040/159 GF40 CP | ALBIS PLASTIC GmbH | PP Homopolymer | ALTECH® PP-H |
| DuraMax™ DMX 8060NC | Advanced Polymer Alloys | TPE | DuraMax™ |
| Polifor® 5003/V2-EP NATURALE | SO.F.TER. SPA | PP Copolymer | Polifor® |