Vectra® E631i
| Category: | LCP , Liquid Crystal Polymer |
| Manufacturer: | Celanese Corporation |
| Trademark: | Vectra® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | D4Vbgc_VectraE631i.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
30% glass reinforced Inherently flame retardant. UL-Listing V-0 black at 0.15mm thickness per UL 94 flame testing. UL = Underwriters Laboratories (USA) |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.61 | g/cm³ | ISO 1183 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 18000 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Break) | 145 | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Break) | 1.3 | % | ISO 527-2/1A/5 |
| Flexural Modulus (23°C) | 17000 | MPa | ISO 178 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 250 | °C | ISO 75-2/A |
| Melting Temperature 1 | 335 | °C | ISO 11357-3 |
| Electrical | Nominal Value | Test Method | |
|---|---|---|---|
| Relative Permittivity | |||
| 1 MHz | 4.50 | IEC 60250 | |
| 2.05 GHz | 7.41 | IPC TM-650 2.5.5.13 | |
| Dissipation Factor (2.05 GHz) | 0.012 | IPC TM-650 2.5.5.13 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (0.150 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 150 | °C | |
| Drying Time | 6.0 | hr | |
| Suggested Max Moisture | 0.010 | % | |
| Hopper Temperature | 20 - 30 | °C | |
| Rear Temperature | 315 - 325 | °C | |
| Middle Temperature | 320 - 330 | °C | |
| Front Temperature | 325 - 335 | °C | |
| Nozzle Temperature | 335 - 345 | °C | |
| Processing (Melt) Temp | 335 - 345 | °C | |
| Mold Temperature | 80 - 120 | °C | |
| Injection Pressure | 50.0 - 150 | MPa | |
| Injection Rate | Fast | ||
| Holding Pressure | 50.0 - 150 | MPa | |
| Back Pressure | 0.00 - 3.00 | MPa |
| Injection instructions |
|---|
| Feed Temperature: 60 to 850°CZone 4 Temperature: 330 to 340°C |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Statimax 820 | Polymics, Ltd. | PBI | Statimax |
| Multi-Flex® TPO D5308 X | Multibase, A Dow Corning Company | TPO (POE) | Multi-Flex® TPO |
| Alathon® M6580WC | LyondellBasell Industries | HDPE | Alathon® |
| Flontech® FT-BRR30-GRN-6 | Guarniflon S.p.A. - Flontech Division | PTFE | Flontech® |
| HiFill® POM HO GF20 A1 | Techmer Engineered Solutions | Acetal (POM) Homopolymer | HiFill® |