Shinko-Lac® ABS HF-3
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Mitsubishi Rayon America Inc. |
| Trademark: | Shinko-Lac® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | D3xGrK_Shinko-Lac-ABS-HF-3.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Shinko-Lac ABS HF-3 is a high flow grade of ABS that is suitable for large or thin products and is effective for the remedies of sink marks, weld lines and molding cycle savings. Other features of HF-3 include an excellent balance of rigidity, strength, processability and glossiness. Typical applications of HF-3 include communications equipment, household goods and appliances. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| UL File Number |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.05 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 4.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.50 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.30 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 108 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2450 | MPa | ASTM D638 |
| Tensile Strength (Yield, 23°C) | 41.2 | MPa | ASTM D638 |
| Flexural Modulus (23°C, 6.35 mm) | 2450 | MPa | ASTM D790 |
| Flexural Strength (Yield, 23°C, 6.35 mm) | 63.7 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -40°C, 6.35 mm | 69 | J/m | ASTM D256 |
| 0°C, 6.35 mm | 120 | J/m | ASTM D256 |
| 23°C, 6.35 mm | 160 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 12.7 mm) | 89.0 | °C | ASTM D648 |
| CLTE - Flow | 8.5E-5 | cm/cm/°C | ASTM D696 |
| Specific Heat | 1670 | J/kg/°C | ASTM C351 |
| Thermal Conductivity | 0.21 | W/m/K | ASTM C177 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (NC) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 85.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.10 | % | |
| Rear Temperature | 180 - 250 | °C | |
| Middle Temperature | 180 - 250 | °C | |
| Front Temperature | 180 - 250 | °C | |
| Mold Temperature | 40.0 - 80.0 | °C | |
| Injection Pressure | 58.8 - 108 | MPa |
| Injection instructions |
|---|
| Higher mold temperature provides a product with excellent surface finish and less residual stress. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 200 GB 23 | RTP Company | Nylon 66 | RTP |
| TUFNYL® RHS NATURAL | SRF Ltd. | Nylon 66 | TUFNYL® |
| TYNE® Olefins W6223 | Tyne Plastics LLC. | PP Homopolymer | TYNE® Olefins |
| Dryflex® 402601S | ELASTO | SBS | Dryflex® |
| ARLEN™ CH245NK | Mitsui Chemicals America, Inc. | Nylon 6T | ARLEN™ |