Bakelite® MP 4165
| Category: | Mel Phenolic , Melamine Phenolic |
| Manufacturer: | Hexion Inc. |
| Trademark: | Bakelite® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | D3mzpu_Bakelite-MP-4165.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Product Description Melamine-phenolic moulding compound, inorganically filled, glass fibre reinforced, good temperature stability, high level of mechanical properties, copper adhesive, flammability UL 94 V-0/1,5 mm (MP 4165-8899-S5), UL 94 V-0 / 1,6 mm (not listed) Application Areas Commutators (fuel pumps, actuators, HVAC motors, fan motors, window lift motors, ABS, wiper motors, garden appliances, household appliances, power tools, universal motors) |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.81 | g/cm³ | ISO 1183 |
| Apparent Density | 0.65 | g/cm³ | ISO 60 |
| Molding Shrinkage | ISO 2577 | ||
| -- 1 | 0.050 | % | |
| -- 2 | 0.10 | % | |
| Water Absorption - 24h/23C | 20.0 | mg | ISO 62 |
| Post Shrinkage | ISO 2577 | ||
| -- 3 | 0.30 | % | |
| -- 4 | 0.25 | % |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Compression Molding Molding Pressure | > 15.0 | MPa | |
| Compression Molding Temperature | 160 to 190 | °C |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 961/30) | 290 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 12500 | MPa | ISO 527-2/1 |
| Tensile Stress | 60.0 | MPa | ISO 527-2/5 |
| Flexural Modulus | 13500 | MPa | ISO 178 |
| Flexural Stress 5 | 110 | MPa | ISO 178 |
| Compressive Stress | 250 | MPa | ISO 604 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength (23°C) | 7.5 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (8.0 MPa, Unannealed) | 135 | °C | ISO 75-2/C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+11 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+12 | ohms·cm | IEC 60093 |
| Electric Strength 6(1.00 mm) | 29 | kV/mm | IEC 60243-1 |
| Relative Permittivity (100 Hz) | 7.50 | IEC 60250 | |
| Dissipation Factor (100 Hz) | 0.10 | IEC 60250 | |
| Comparative Tracking Index (Solution A) | 300 | V | IEC 60112 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 60.0 to 75.0 | °C | |
| Nozzle Temperature | 80.0 to 100 | °C | |
| Processing (Melt) Temp | 80.0 to 100 | °C | |
| Mold Temperature | 160 to 190 | °C | |
| Injection Pressure | > 15.0 | MPa | |
| Back Pressure | 0.500 to 2.00 | MPa |
| Note Message | |
|---|---|
| 1 . | Compression |
| 2 . | Injection |
| 3 . | Injection |
| 4 . | Compression |
| 5 . | 2.0 mm/min |
| 6 . | short term, electrode layout P25mm/P25mm in transformer oil equivalent to IEC 60296 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NORYL GTX™ GTX934 resin | SABIC Innovative Plastics Asia Pacific | PPE+PS+Nylon | NORYL GTX™ |
| BioCeres® BC-LBI01 | FuturaMat | Biodeg Polymers | BioCeres® |
| Electrafil® PA6/6 CF18 BK | Techmer Engineered Solutions | Nylon 66 | Electrafil® |
| EMERGE™ PC 4701-15 | Trinseo | PC | EMERGE™ |
| Karina WHITE PVC COMPOUND 802D10/ 1-E-AC | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |