Estane® 2103-80AE TPU
| Category: | TPU-Polyether , Thermoplastic Polyurethane Elastomer (Polyether) |
| Manufacturer: | Lubrizol Advanced Materials, Inc. |
| Trademark: | Estane® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | D3gvdh_Estane-2103-80AE-TPU.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 2103-80AE is a thermoplastic polyurethane elastomer. |
| General Information | |
|---|---|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.13 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (224°C/1.2 kg) | 40 | g/10 min | ASTM D1238 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | -0.20 - 0.50 | % | ASTM D955 |
| Transverse flow | 0.60 - 0.80 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 82 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Taber Abrasion Resistance (1000 g, H-22 Wheel) | 20.0 | mg | ASTM D1044 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412 | ||
| 50% strain, 3.20mm | 4.10 | MPa | ASTM D412 |
| 100% strain, 3.20mm | 5.50 | MPa | ASTM D412 |
| 300% strain, 3.20mm | 11.7 | MPa | ASTM D412 |
| Tensile Strength (Break, 3.20 mm) | 34.5 | MPa | ASTM D412 |
| Tensile Elongation (Break, 3.20 mm) | 600 | % | ASTM D412 |
| Tensile Elongation at Break (3.20 mm) | 70 | % | ASTM D412 |
| Tear Strength 1(3.20 mm) | 105 | kN/m | ASTM D624 |
| Compression Set | ASTM D395B | ||
| 25°C, 22 hr | 30 | % | ASTM D395B |
| 70°C, 22 hr | 33 | % | ASTM D395B |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | -40.0 | °C | DSC |
| Vicat Softening Temperature | 85.0 | °C | ASTM D1525 2 |
| CLTE - Flow | 1.7E-4 | cm/cm/°C | ASTM D696 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.0 - 93.0 | °C | |
| Processing (Melt) Temp | 182 - 210 | °C | |
| Mold Temperature | 16.0 - 60.0 | °C |
| Injection instructions |
|---|
| Air Dew Point: <-40°C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.0 - 93.0 | °C | |
| Melt Temperature | 182 - 199 | °C |
| Extrusion instructions |
|---|
| Air Dew Point: <-40°C |
| Note Message | |
|---|---|
| 1 . | C mould |
| 2 . | 标准 B (120°C/h), 压 力1 (10N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Armlen® PP SM 20-2UP | Poly Plastic | PP, Unspecified | Armlen® |
| ECOGRAN® PA66 DEMI DULL | Eurocompound Polymers | Nylon 66 | ECOGRAN® |
| Ingeo™ 6201D | NatureWorks® LLC | PLA | Ingeo™ |
| LUVOCOM® 80/TF/18/SI/2-3 | Lehmann & Voss & Co. | Acetal (POM) Copolymer | LUVOCOM® |
| Edgetek™ PC-20GF/000 FR BLK | PolyOne Corporation | PC | Edgetek™ |