Hytrel® HTR8163HVBK
| Category: | TPC-ET , THERMOPLASTIC POLYESTER ELASTOMER |
| Manufacturer: | DuPont Performance Polymers |
| Trademark: | Hytrel® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | D2piKd_Hytrel-HTR8163HVBK.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 65 Shore D Polyester Elastomer with Heat Ageing Protection Developed for Extrusion |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Part Marking Code (ISO 11469) |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.23 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 5.0 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (230°C/2.16 kg) | 5.00 | cm³/10min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness | ISO 868 | ||
| Shore D | 65 | ||
| Shore D, 15 sec | 60 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 350 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | ||
| Yield | 21.0 | MPa | |
| Break | 44.0 | MPa | |
| 5.0% Strain | 12.0 | MPa | |
| 10% Strain | 17.8 | MPa | |
| 50% Strain | 20.0 | MPa | |
| 100% Strain | 23.0 | MPa | |
| 300% Strain | 32.0 | MPa | |
| Tensile Strain | ISO 527-2 | ||
| Yield | 30 | % | |
| Break | > 300 | % | |
| Tensile Creep Modulus | ISO 899-1 | ||
| 1 hr | 310 | MPa | |
| 1000 hr | 260 | MPa | |
| Flexural Modulus | 374 | MPa | ISO 178 |
| Abrasion Resistance | 110 | mm³ | ISO 4649 |
| Fill Analysis | Nominal Value | Unit | |
|---|---|---|---|
| Specific Heat Capacity of Melt | 2090 | J/kg/°C | |
| Thermal Conductivity of Melt | 0.16 | W/m/K |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength - Flow | 180 | kN/m | ISO 34-1 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -40°C | 8.5 | kJ/m² | |
| -30°C | 12 | kJ/m² | |
| 23°C, Partial Break | 130 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/1A | ||
| -50°C | 10 | kJ/m² | |
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | -70.0 | °C | ISO 974 |
| Melting Temperature 1 | 211 | °C | ISO 11357-3 |
| Fill Analysis | Nominal Value | Unit | |
|---|---|---|---|
| Melt Density | 1.04 | g/cm³ |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tenac™-C 7520 | Asahi Kasei Chemicals Corporation | Acetal (POM) Copolymer | Tenac™-C |
| Mowiflex™ FX 407 | Kuraray Co., Ltd. | PVOH | Mowiflex™ |
| Monprene® IN-12250 | Teknor Apex Company | TPE | Monprene® |
| Lion Idemitsu Composites PPS Y551F1 | Lion Idemitsu Composites Co., Ltd. | PPS | Lion Idemitsu Composites PPS |
| ADENE® B36KYB-00 | A.D. Compound S.p.A. | PP Homopolymer | ADENE® |