LNP™ VERTON™ NV004E compound
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ VERTON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | D2TG9h_LNP-VERTON-NV004E-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP VERTON* NV004E is a compound based on PC+ABS Blend resin containing 20% Long Glass Fiber. Added features of this material include: Easy Molding, Structural. Also known as: LNP* VERTON* Compound PCA-F-7004 EM Product reorder name: NV004E |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.30 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | ASTM D955, ISO 294-4 | ||
| Flow : 24 hr | 0.20 to 0.40 | % | |
| Across Flow : 24 hr | 0.20 to 0.40 | % | |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.10 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 6620 | MPa | ASTM D638 |
| -- | 7800 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break | 119 | MPa | ASTM D638 |
| Break | 125 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Break | 2.4 | % | ASTM D638 |
| Break | 2.1 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 5670 | MPa | ASTM D790 |
| -- | 6980 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 160 | MPa | ASTM D790 |
| -- | 140 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| -40°C | 170 | J/m | ASTM D256 |
| 23°C | 160 | J/m | ASTM D256 |
| -40°C 2 | 18 | kJ/m² | ISO 180/1A |
| 23°C 3 | 18 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 570 | J/m | ASTM D4812 |
| 23°C 4 | 41 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact (23°C, Energy at Peak Load) | 16.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 134 | °C | ASTM D648 |
| CLTE | |||
| Flow : -40 to 40°C | 4.3E-5 | cm/cm/°C | ASTM E831 |
| Flow : -40 to 40°C | 4.5E-5 | cm/cm/°C | ISO 11359-2 |
| Transverse : -40 to 40°C | 4.7E-5 | cm/cm/°C | ASTM E831 |
| Transverse : -40 to 40°C | 4.8E-5 | cm/cm/°C | ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 to 93.3 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.040 | % | |
| Rear Temperature | 260 to 271 | °C | |
| Middle Temperature | 271 to 282 | °C | |
| Front Temperature | 282 to 293 | °C | |
| Processing (Melt) Temp | 277 to 288 | °C | |
| Mold Temperature | 60.0 to 93.3 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® LDPE 2404AF00 | Saudi Basic Industries Corporation (SABIC) | LDPE | SABIC® LDPE |
| Nanjing Hongrui PA66 A1304 | Nanjing Hongrui Engineering Plastics Co., Ltd. | Nylon 66 | Nanjing Hongrui PA66 |
| LEXAN™ ML3999 resin | SABIC Innovative Plastics Europe | PC | LEXAN™ |
| OPNYL OP66GF33 | Ovation Polymers Inc. | Nylon 66 | OPNYL |
| Optix® CP-61 | Plaskolite West, Inc. | Acrylic (PMMA) | Optix® |