Witcom PEI 6G/3L1
| Category: | PEI , Polyether Imide |
| Manufacturer: | Witcom Engineering Plastics B.V. |
| Trademark: | Witcom PEI |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | D1uE2l_Witcom-PEI-6G-3L1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Witcom PEI 6G/3L1 is a polyetherimide (PEI) product that contains a 30% glass fiber reinforced material. It can be processed by injection molding and is available in Europe. Features include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.61 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow (3.00 mm) | 0.20 - 0.40 | % | ISO 2577 |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 0.80 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.40 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break) | 165 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 1.0 - 3.0 | % | ISO 527-2 |
| Flexural Modulus | 8500 | MPa | ISO 178 |
| Flexural Stress | 210 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 10 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength | 30 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 210 | °C | ISO 75-2/A |
| CLTE - Flow | 2.1E-5 | cm/cm/°C | ISO 11359-2 |
| RTI Imp (3.00 mm) | 170 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+15 | ohms | ASTM D257 |
| Comparative Tracking Index | 150 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.800 mm) | V-0 | ISO 1210 | |
| Glow Wire Flammability Index (1.60 mm) | 960 | °C | IEC 60695-2-12 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 150 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Processing (Melt) Temp | 370 - 410 | °C | |
| Mold Temperature | 140 - 180 | °C | |
| Injection Rate | Fast | ||
| Back Pressure | 0.00 - 1.00 | MPa |
| Injection instructions |
|---|
| Screw speed: 0.1 - 0.2 m/sInjection pressure: Keep to a minimumHold pressure: Keep to a minimum |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MARCOBLEND AU 2000 Sx Series | POLY GIN | PC | MARCOBLEND |
| TECHNYL® C 218 V30 BLACK | Solvay Engineering Plastics | Nylon 6 | TECHNYL® C |
| BRALEN® FB 3-33 | Slovnaft Petrochemicals, s.r.o. | LDPE | BRALEN® |
| POLYFLON™ D-2C | DAIKIN AMERICA, INC. | PTFE | POLYFLON™ |
| Sylvin 83014-95FU Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |