Telcar® TL-8451
| Category: | TPE , Thermoplastic Elastomer |
| Manufacturer: | Teknor Apex Company |
| Trademark: | Telcar® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | D1rCDU_Telcar-TL-8451.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Telcar TL-8451 is a high performance, halogen-free thermoplastic elastomer designed for electrical applications requiring flexibility over a wide temperature range. Telcar TL-8451 is a high durometer grade that is UV stabilized and RoHS compliant. This grade is UL listed and is suitable for both injection molding and extrusion. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Wire Types |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| UL File Number |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.998 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 20 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 84 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deformation Under Load 1(150°C) | 6.00 | % | ASTM D621 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 2 | ASTM D412 | ||
| 100% strain, 0.508mm 3 | 4.52 | MPa | ASTM D412 |
| 300% strain, 0.508mm 4 | 6.21 | MPa | ASTM D412 |
| Tensile Strength (fracture, 0.508mm) | 16.5 | MPa | ASTM D412 |
| Tensile Elongation (fracture, 0.508mm) | 660 | % | ASTM D412 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength in Air (136°C, 168 hr) | 4.0 | % | ASTM D573 |
| Change in Ultimate Elongation in Air (136°C, 168 hr) | -8.0 | % | ASTM D573 |
| Change in Tensile Strength (60°C, 168 hr, in IRM 902 Oil) | -14 | % | ASTM D471 |
| Change in Ultimate Elongation (60°C, 168 hr, in IRM 902 Oil) | -7.0 | % | ASTM D471 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Continuous Use Temperature | 105 | °C | UL 1581 |
| Brittleness Temperature | < -60.0 | °C | ASTM D746 |
| RTI Elec | 90.0 | °C | UL 746 |
| RTI | 90.0 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity (50°C) | 9.6E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength | 38 | kV/mm | ASTM D149 |
| Dielectric Constant | ASTM D150 | ||
| 1 kHz | 2.10 | ASTM D150 | |
| 1 MHz | 2.33 | ASTM D150 | |
| Dissipation Factor | ASTM D150 | ||
| 1 kHz | 2.0E-4 | ASTM D150 | |
| 1 MHz | 1.0E-4 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.810 mm, All Colors) | HB | UL 94 | |
| Oxygen Index | 18 | % | ASTM D2863 |
| Additional Information |
|---|
| 最高连续工作温度，UL-1581：105°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 199 - 216 | °C | |
| Middle Temperature | 213 - 221 | °C | |
| Front Temperature | 221 - 227 | °C | |
| Nozzle Temperature | 221 - 229 | °C | |
| Processing (Melt) Temp | 221 - 229 | °C | |
| Mold Temperature | 25.0 - 65.6 | °C | |
| Injection Pressure | 1.38 - 6.89 | MPa | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 0.172 - 0.345 | MPa | |
| Screw Speed | 50 - 100 | rpm | |
| Cushion | 3.81 - 25.4 | mm |
| Injection instructions |
|---|
| 无需干燥。但如果湿度过大，则将粒料在150°F (65°C)的温度下干燥2-4小时。 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 193 - 210 | °C | |
| Cylinder Zone 2 Temp. | 199 - 216 | °C | |
| Cylinder Zone 3 Temp. | 213 - 221 | °C | |
| Cylinder Zone 5 Temp. | 221 - 227 | °C | |
| Die Temperature | 221 - 229 | °C |
| Extrusion instructions |
|---|
| 螺杆转速30 - 100 rpm |
| Note Message | |
|---|---|
| 1 . | Weight 2000 grams |
| 2 . | die cut from extruded tapes |
| 3 . | Mouth die C, 510mm/min |
| 4 . | C mold, 510mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MALAT 04G192 NAT | AD majoris | Polyester, TP | MALAT |
| TEREZ PA 6.6 HT 7500 GF 40 | TER HELL PLASTIC GMBH | Nylon 66 | TEREZ PA 6.6 |
| LCA® N66-101 Type | UniPlas, Inc. | Nylon 66 | LCA® |
| Karina GRAY PVC COMPOUND 960-18/431-IS-AS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Sylvin 6423-83 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |