Clariant PC PC-1100
| Category: | PC , Polycarbonate |
| Manufacturer: | Clariant Corporation |
| Trademark: | Clariant PC |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | D1fOzP_Clariant-PC-PC-1100.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Clariant PC PC-1100 is a polycarbonate (PC) material,. This product is available in North America and is processed by injection molding. The main features of Clariant PC PC-1100 are:
Typical application areas include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.60 | % | ASTM D955 |
| Water Absorption | ASTM D570 | ||
| 24 hr | 0.15 | % | ASTM D570 |
| Saturation | 0.35 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 78 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 62.1 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 90 | % | ASTM D638 |
| Flexural Modulus | 2280 | MPa | ASTM D790 |
| Flexural Strength | 93.1 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm) | 800 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 132 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 129 | °C | ASTM D648 |
| CLTE - Flow | 1.3E-4 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength | 15 | kV/mm | ASTM D149 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | V-2 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 304 - 343 | °C | |
| Middle Temperature | 304 - 343 | °C | |
| Front Temperature | 304 - 343 | °C | |
| Processing (Melt) Temp | 304 - 327 | °C | |
| Melt Temperature (Aim) | 316 | °C | |
| Mold Temperature | 82.2 - 121 | °C | |
| Injection Rate | Fast | ||
| Back Pressure | 0.345 - 0.689 | MPa | |
| Screw Speed | 45 - 75 | rpm | |
| Cushion | 3.18 - 6.35 | mm |
| Injection instructions |
|---|
| The minimum injection pressure required to fill the part should be used for the first stage. The hold pressure should be set between 50% and 75% of the injection pressure. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 800 TFE 5 SI 2 HB | RTP Company | Acetal (POM) Copolymer | RTP |
| TechnoMid A225 FL | TechnoCompound GmbH | Nylon 66 | TechnoMid |
| Spartech Polycom X02435 | Spartech Polycom | PPE | Spartech |
| Vydyne® 21SPF1 | Ascend Performance Materials Operations LLC | Nylon 66 | Vydyne® |
| AKROMID® B3 GFM 15/25 natural (3578) | AKRO-PLASTIC GmbH | Nylon 6 | AKROMID® |