Lotryl® 18MA02
| Category: | EMA , Ethylene Methyl Acrylate Copolymer |
| Manufacturer: | Arkema |
| Trademark: | Lotryl® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | D1TpEq_Lotryl-18MA02.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LOTRYL® 18MA02 is a random copolymer of Ethylene and Methyl Acrylate produced by high-pressure radicalar polymerization process. Applications Due to the methyl acrylate content, LOTRYL® 18MA02 can be used for applications where softness, flexibility and polarity are required. Typical applications are extrusion coating, coextrusion and compounds. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.940 | g/cm³ | ISO 1183, ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.0 to 3.0 | g/10 min | ASTM D1238, ISO 1133 |
| Methyl Acrylate Content | 17.0 to 20.0 | wt% |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, Compression Molded) | 25 | ASTM D2240, ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break, Compression Molded) | 13.0 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break, Compression Molded) | 700 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus (Compression Molded) | 50.0 | MPa | ASTM D790, ISO 178 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 53.0 | °C | ISO 306/A, ASTM D1525 1 |
| Melting Temperature | 83.0 | °C | ISO 11357-3 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 150 to 170 | °C | |
| Cylinder Zone 2 Temp. | 170 | °C | |
| Cylinder Zone 3 Temp. | 170 | °C | |
| Cylinder Zone 4 Temp. | 170 | °C | |
| Die Temperature | 170 | °C |
| Note Message | |
|---|---|
| 1 . | Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TIPPLEN® H 145 F | MOL Petrochemicals Co. Ltd. | PP Homopolymer | TIPPLEN® |
| NILAMID® A3 W GF55 | Nilit Plastics | Nylon 66 | NILAMID® |
| Monprene® IN-22059 | Teknor Apex Company | TPE | Monprene® |
| Rotec® ABS 1002 FR V0/5 | ROMIRA GmbH | ABS | Rotec® ABS |
| Durethan® AKV 325 H2.0 901510 | LANXESS GmbH | Nylon 66 | Durethan® |