Next Nylon 66 Prime Series PGF50-01NC
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Next Polymers Ltd. |
| Trademark: | Next Nylon 66 Prime Series |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | D115gC_Next-Nylon-66-Prime-Series-PGF50-01NC.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Description PA66 Glass Fiber Reinforced FR Natural Compound Product Applications This product is ideally suited for Appliances, Industrial control, Power distribution application such as MCCB and Connectors & The long term thermal performance of this grade also make it ideal where it can with stand temperature of 165 Deg.c for over 6000 Hrs. Benefits This Halogen & Red phosphorous Free flamme retardent grade combines excellent all round mechanical properties, Long term Thermal performance with outstanding flame retardency and Electrical prformance. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.64 | -- | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | |||
| Flow | 0.20 | -- | % | |
| Across Flow | 0.45 | -- | % | |
| Water Absorption | ASTM D570 | |||
| 23°C, 24 hr | 0.80 | -- | % | |
| Saturation 1 | 5.5 | -- | % |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness | ASTM D785 | |||
| M-Scale | 110 | -- | ||
| R-Scale | 125 | -- |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 12500 | 9500 | MPa | ASTM D638 |
| Tensile Strength | 180 | 135 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 3.0 | 5.0 | % | ASTM D638 |
| Flexural Modulus | 11000 | 8500 | MPa | ASTM D790 |
| Flexural Strength | 250 | 210 | MPa | ASTM D790 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact (23°C) | 110 | 150 | J/m | ASTM D256 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | |||
| 0.45 MPa, Unannealed | 260 | -- | °C | |
| 1.8 MPa, Unannealed | 255 | -- | °C | |
| Melting Temperature | 263 | -- | °C | ASTM D2117 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+14 | -- | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+17 | -- | ohms·cm | IEC 60093 |
| Electric Strength | 32 | -- | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 0.800 mm | V-0 | -- | ||
| 1.60 mm | V-0 | -- | ||
| Glow Wire Flammability Index | IEC 60695-2-12 | |||
| 0.800 mm | 960 | -- | °C | |
| 1.60 mm | 960 | -- | °C | |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | |||
| 0.800 mm | 775 | -- | °C | |
| 1.60 mm | 775 | -- | °C |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature - Hot Air Dryer | 80.0 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 260 to 270 | °C | |
| Middle Temperature | 270 to 280 | °C | |
| Front Temperature | 270 to 280 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C |
| Note Message | |
|---|---|
| 1 . | Immersed |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ExxonMobil™ HDPE HYA 800 | ExxonMobil Chemical | HDPE, UHMW | ExxonMobil™ HDPE |
| LNP™ STAT-KON™ RFD02 compound | SABIC Innovative Plastics | Nylon 66 | LNP™ STAT-KON™ |
| Lupox® GP2056F | LG Chem Ltd. | PBT | Lupox® |
| Daelim Po1y® 5502HSUV | DAELIM INDUSTRIAL CO., LTD. | HDPE | Daelim Po1y® |
| Telcar® TL-8730A | Teknor Apex Company | TPE | Telcar® |