Sarlink® TPV 3170
| Category: | TPV , Thermoplastic Vulcanizate |
| Manufacturer: | Teknor Apex Company |
| Trademark: | Sarlink® TPV |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | D0gfKW_Sarlink-TPV-3170.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| SARLINK® 3170 is a multi-purpose thermoplastic elastomer featuring excellent compression set, heat resistance and weatherability. SARLINK® 3170 can be processed by injection molding, blow mounding or extrusion for applications such as seals, gaskets, chemical resistant hose and tube, heat resistant boots and bellows. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 0.948 | g/cm³ | ASTM D792 |
| -- | 0.950 | g/cm³ | ISO 1183 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240, ISO 868 | ||
| Shaw A, 5 seconds, extruded | 71 | ASTM D2240, ISO 868 | |
| Shore A, 5 seconds, injection molding | 75 | ASTM D2240, ISO 868 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412, ISO 37 | ||
| Transverse flow : 100% strain | 3.30 | MPa | ASTM D412, ISO 37 |
| Flow : 100% strain | 5.10 | MPa | ASTM D412, ISO 37 |
| Tensile Strength | |||
| Transverse flow : Fracture | 7.72 | MPa | ASTM D412 |
| Flow : Fracture | 6.70 | MPa | ASTM D412, ISO 37 |
| Transverse flow : Fracture | 7.70 | MPa | ISO 37 |
| Tensile Elongation | ASTM D412, ISO 37 | ||
| Transverse flow : Fracture | 670 | % | ASTM D412, ISO 37 |
| Flow : Fracture | 300 | % | ASTM D412, ISO 37 |
| Tear Strength - Across Flow | |||
| -- | 42.0 | kN/m | ASTM D624 |
| -- 1 | 42 | kN/m | ISO 34-1 |
| Compression Set | ASTM D395, ISO 815 | ||
| 23°C, 22 hr | 25 | % | ASTM D395, ISO 815 |
| 70°C, 22 hr | 43 | % | ASTM D395, ISO 815 |
| 125°C, 70 hr | 63 | % | ASTM D395, ISO 815 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength in Air - Across Flow | |||
| 135°C, 1000 hr | -8.0 | % | ASTM D573, ISO 188 |
| 100% strain, 135°C, 1000 hr | 10 | % | ASTM D573 |
| 150°C, 168 hr | -4.0 | % | ASTM D573, ISO 188 |
| 100% strain, 150°C, 168 hr | 5.0 | % | ASTM D573 |
| 100% strain 135°C, 1000 hr | 10 | % | ISO 188 |
| 100% strain 150°C, 168 hr | 5.0 | % | ISO 188 |
| Change in Ultimate Elongation in Air - Across Flow | ASTM D573, ISO 188 | ||
| 135°C, 1000 hr | -13 | % | ASTM D573, ISO 188 |
| 150°C, 168 hr | -14 | % | ASTM D573, ISO 188 |
| Change in Durometer Hardness in Air | ASTM D573, ISO 188 | ||
| Support a, 135°C, 1000 hr | -1.0 | ASTM D573, ISO 188 | |
| Support a, 150°C, 168 hr | 3.0 | ASTM D573, ISO 188 | |
| Change in Volume | |||
| 125°C, 70 hr, in IRM 903 oil | 120 | % | ASTM D471 |
| 125°C, 70 hr, in IRM 903 oil | 120 | % | ISO 1817 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| RTI Elec | 50.0 | °C | UL 746 |
| RTI Imp | 50.0 | °C | UL 746 |
| RTI | 50.0 | °C | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm, Natural and Black Colors) | HB | UL 94 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Apparent Shear Viscosity - Capillary, @ 206/s | |||
| 200°C | 290 | Pa·s | ISO 11443 |
| 200°C | 290 | Pa·s | ASTM D3835 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 180 - 215 | °C | |
| Middle Temperature | 180 - 215 | °C | |
| Front Temperature | 180 - 215 | °C | |
| Nozzle Temperature | 187 - 220 | °C | |
| Processing (Melt) Temp | 185 - 220 | °C | |
| Mold Temperature | 10.0 - 55.0 | °C | |
| Back Pressure | 0.100 - 1.00 | MPa | |
| Screw Speed | 100 - 200 | rpm |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 180 - 200 | °C | |
| Cylinder Zone 2 Temp. | 180 - 205 | °C | |
| Cylinder Zone 3 Temp. | 187 - 210 | °C | |
| Cylinder Zone 4 Temp. | 187 - 210 | °C | |
| Melt Temperature | 195 - 215 | °C | |
| Die Temperature | 195 - 215 | °C | |
| Take-Off Roll | 20.0 - 50.0 | °C |
| Extrusion instructions |
|---|
| Screen Pack: 20 to 60 meshScrew: general purposeCompression Ratio: 3:1 |
| Note Message | |
|---|---|
| 1 . | Method B, right-angle specimen (without cut) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Arak LLDPE LL0220AA | Shazand (Arak) Petrochemical Corporation | LLDPE | Arak LLDPE |
| Formolene® HP4000 | Formosa Plastics Corporation, U.S.A. | HDPE | Formolene® |
| Geon™ Duracap™ L4605 Green 5765 | PolyOne Corporation | PVC, Semi-Rigid | Geon™ Duracap™ |
| Karina IVORY PVC COMPOUND -E 851-35/ 1-E-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Sylvin 8887-95 Brown 7400 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |