VAMPTER C 3028 V0
| Category: | PC+PBT , Polycarbonate + PBT |
| Manufacturer: | Vamp Tech |
| Trademark: | VAMPTER |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | D0UCvf_VAMPTER-C-3028-V0.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| UL 94 V0, blend PC/PBT 30% glass fiber reinforced, halogen free, good dimensional stability, good mechanical properties, very low toxicity and smoke |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.52 | g/cm³ | ASTM D792 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 8000 | MPa | ASTM D638 |
| Tensile Strength (Yield) | 90.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 2.0 | % | ASTM D638 |
| Flexural Modulus | 7000 | MPa | ASTM D790 |
| Flexural Strength | 120 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | 7.0 | kJ/m² | ISO 180/A |
| Unnotched Izod Impact Strength | 35 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 160 | °C | ASTM D648A |
| Vicat Softening Temperature | 140 | °C | ASTM D1525 1 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | V-0 | ||
| 3.20 mm | V-0 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 260 | °C | |
| Mold Temperature | 70.0 | °C |
| Note Message | |
|---|---|
| 1 . | Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SEQUEL® 1780 | LyondellBasell Industries | TPO (POE) | SEQUEL® |
| Ultradur® B 4300 G6 LS High Speed BK15045 | BASF Corporation | PBT | Ultradur® |
| CP PRYME® Nylon 66 NN200HSL | Chase Plastics Services Inc. | Nylon 66 | CP PRYME® Nylon 66 |
| Karina YELLOW PVC COMPOUND -E 530-02/167-A-IS-SD (C900) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LNP™ LUBRICOMP™ OFL36A compound | SABIC Innovative Plastics | PPS | LNP™ LUBRICOMP™ |