LNP™ LUBRICOMP™ KA000M compound
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | D0Og9A_LNP-LUBRICOMP-KA000M-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP KA000M is a compound based on Acetal Copolymer resin containg Aramide and Proprietary Lubricant. Added features include Internally Lubricated. Also known as: LNP* LUBRICOMP* Compound LUBRICOMP-KA Product reorder name: KA000M |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.36 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (315°C/5.0 kg) | 4.00 to 6.00 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow | 2.5 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2600 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 41.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Yield) | 7.4 | % | ISO 527-2/5 |
| Flexural Modulus 1 | ISO 178 | ||
| -- | 2300 | MPa | |
| 60°C | 1400 | MPa | |
| 100°C | 800 | MPa | |
| Flexural Stress | ISO 178 | ||
| -- | 68.0 | MPa | |
| 60°C | 42.0 | MPa | |
| 100°C | 22.0 | MPa | |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.21 | ||
| vs. Itself - Static | 0.21 | ||
| Flexural Strain at Break 2 | ISO 178 | ||
| -- | 7.0 | % | |
| 60°C | 7.0 | % | |
| 100°C | 7.0 | % | |
| Wear Factor - Washer | 9.00 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength 3(23°C) | 3.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 4(23°C) | 25 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 5(1.8 MPa, Unannealed, 64.0 mm Span) | 92.0 | °C | ISO 75-2/Af |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 60°C | 1.1E-4 | cm/cm/°C | |
| Transverse : 23 to 60°C | 1.2E-4 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 177 to 188 | °C | |
| Middle Temperature | 193 to 204 | °C | |
| Front Temperature | 210 to 221 | °C | |
| Processing (Melt) Temp | 199 to 216 | °C | |
| Mold Temperature | 82.2 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2 mm/min |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Flontech® FT-BRR40-6 | Guarniflon S.p.A. - Flontech Division | PTFE | Flontech® |
| Gallonprene® GP210-9002L | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| HiFill® PC GF20 | Techmer Engineered Solutions | PC | HiFill® |
| LightSpan® LS-3440 | NuSil Technology | Silicone | LightSpan® |
| Sylvin 8250-70 Brown 7460 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |