Shinko-Lac® ASA TW15
| Category: | ASA , Acrylonitrile Styrene Acrylate |
| Manufacturer: | Mitsubishi Rayon America Inc. |
| Trademark: | Shinko-Lac® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | CzsyCS_Shinko-Lac-ASA-TW15.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Shinko-Lac® ASA TW15 is an Acrylonitrile Styrene Acrylate (ASA) material. It is available in North America for injection molding. Important attributes of Shinko-Lac® ASA TW15 are:
|
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.06 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (220°C/5.0 kg) | 0.30 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.50 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 99 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, 23°C) | 41.2 | MPa | ASTM D638 |
| Flexural Modulus (23°C) | 2060 | MPa | ASTM D790 |
| Flexural Strength (Yield, 23°C) | 60.8 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 160 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 6.35 mm, Injection Molded | 106 | °C | |
| 1.8 MPa, Unannealed, 6.35 mm, Injection Molded | 93.0 | °C | |
| Vicat Softening Temperature | 107 | °C | ISO 306/B |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Scolefin 34 G 10-0 | Ravago Group | PP Homopolymer | Scolefin |
| Spartech Polycom F5134T2-4 | Spartech Polycom | PP Homopolymer | Spartech |
| BMC 800 | Bulk Molding Compounds, Inc. | Polyester, TS | BMC |
| Cheng Yu FV30G20 | Cheng Yu Plastic Company Limited | Acetal (POM) Homopolymer | Cheng Yu |
| Braskem PP H 614 | Braskem | PP Homopolymer | Braskem PP |