Laticonther 80 GCE/650
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | LATI S.p.A. |
| Trademark: | Laticonther |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | CzlaU4_Laticonther-80-GCE-650.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
High thermal conductivity product based on Polyphenylene Sulphide (PPS). Glass fibres / Mineral filler. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.91 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow : 2.00 mm | 0.15 to 0.30 | % | |
| Flow : 2.00 mm | 0.10 to 0.20 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ISO 527-2/1 | ||
| 23°C | 23000 | MPa | |
| 60°C | 20000 | MPa | |
| 90°C | 18000 | MPa | |
| 120°C | 13000 | MPa | |
| 150°C | 8000 | MPa | |
| Tensile Stress | ISO 527-2/5 | ||
| Break, 23°C | 145 | MPa | |
| Break, 60°C | 130 | MPa | |
| Break, 90°C | 115 | MPa | |
| Break, 120°C | 75.0 | MPa | |
| Break, 150°C | 60.0 | MPa | |
| Tensile Strain | ISO 527-2/5 | ||
| Break, 23°C | 0.80 | % | |
| Break, 60°C | 1.1 | % | |
| Break, 90°C | 1.2 | % | |
| Break, 120°C | 2.0 | % | |
| Break, 150°C | 2.5 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 5.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 15 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact (23°C, 3.20 mm) | 60 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 285 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 275 | °C | ISO 75-2/A |
| Continuous Use Temperature 2 | 225 | °C | |
| Vicat Softening Temperature | 260 | °C | ISO 306/B50 |
| CLTE - Flow (30 to 100°C) | 4.0E-6 | cm/cm/°C | ASTM D696 |
| Thermal Conductivity | 0.90 | W/m/K | ASTM E1952-01 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 to 130 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 290 to 320 | °C | |
| Mold Temperature | 130 to 140 | °C | |
| Injection Rate | Moderate-Fast |
| Note Message | |
|---|---|
| 1 . | at 60 Mpa of cavity pressure |
| 2 . | 20,000 hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Zhongfa PET G30S | Yuyao Zhongfa Engineering Plastics Co. Ltd. | PET | Zhongfa |
| ALFATER XL® A80I 3EF0001 | ALBIS PLASTIC GmbH | TPV | ALFATER XL® |
| Geon™ Vinyl Wire & Cable W2403L | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Wire & Cable |
| Kumho SAN SAN 310TR | Korea Kumho Petrochemical Co., Ltd. | SAN | Kumho SAN |
| LNP™ VERTON™ MV006SU compound | SABIC Innovative Plastics | PP, Unspecified | LNP™ VERTON™ |