SCHULAMID® 6 NV 12 FR
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | A. Schulman Europe |
| Trademark: | SCHULAMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Cz6BC4_SCHULAMID-6-NV-12-FR.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Low viscosity flame-retardant Polyamide 6 grade; halogen and phosphorus-free |
| General Information | |
|---|---|
| Features |
|
| UL File Number |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.15 | -- | g/cm³ | ISO 1183/A |
| Viscosity Number | 130 | -- | cm³/g | ISO 307 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 4200 | 1400 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Yield) | 70.0 | 40.0 | MPa | ISO 527-2/1A/50 |
| Tensile Strain (Yield) | 4.0 | 15 | % | ISO 527-2/1A/50 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 3.5 | 5.0 | kJ/m² | |
| 23°C | 4.0 | 15 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | No Break | No Break | ||
| 23°C | No Break | No Break |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 200 | -- | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed | 90.0 | -- | °C | ISO 75-2/Af |
| Vicat Softening Temperature | ||||
| -- | 218 | -- | °C | ISO 306/A50 |
| -- | 203 | -- | °C | ISO 306/B50 |
| Ball Pressure Test (200°C) | Pass | -- | IEC 60695-10-2 | |
| RTI Elec | UL 746 | |||
| 0.750 mm | 130 | -- | °C | |
| 1.50 mm | 130 | -- | °C | |
| 3.00 mm | 130 | -- | °C | |
| RTI Imp | UL 746 | |||
| 0.750 mm | 75.0 | -- | °C | |
| 1.50 mm | 75.0 | -- | °C | |
| 3.00 mm | 80.0 | -- | °C | |
| RTI Str | UL 746 | |||
| 0.750 mm | 95.0 | -- | °C | |
| 1.50 mm | 95.0 | -- | °C | |
| 3.00 mm | 95.0 | -- | °C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | > 1.0E+12 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+13 | > 1.0E+10 | ohms·cm | IEC 60093 |
| Comparative Tracking Index | 600 | -- | V | IEC 60112 |
| High Amp Arc Ignition (HAI) | UL 746 | |||
| 0.750 mm | PLC 3 | -- | ||
| 1.50 mm | PLC 3 | -- | ||
| 3.00 mm | PLC 2 | -- | ||
| Hot-wire Ignition (HWI) | UL 746 | |||
| 19.1 mm | PLC 0 | -- | ||
| 38.1 mm | PLC 0 | -- | ||
| 76.2 mm | PLC 0 | -- |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate | ISO 3795 | |||
| 0.750 mm, Self-Extinguishing | 0.0 | -- | mm/min | |
| 1.50 mm, Self-Extinguishing | 0.0 | -- | mm/min | |
| 3.00 mm, Self-Extinguishing | 0.0 | -- | mm/min | |
| Flame Rating | UL 94, IEC 60695-11-10, -20 | |||
| 0.380 mm | V-0 | -- | ||
| 0.750 mm | V-0 | -- | ||
| 1.50 mm | V-0 | -- | ||
| 3.00 mm | V-0 | -- | ||
| Glow Wire Flammability Index | IEC 60695-2-12 | |||
| 0.380 mm | 960 | -- | °C | |
| 0.750 mm | 960 | -- | °C | |
| 1.50 mm | 960 | -- | °C | |
| 3.00 mm | 960 | -- | °C | |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | |||
| 0.380 mm | 750 | -- | °C | |
| 1.50 mm | 750 | -- | °C | |
| 3.00 mm | 750 | -- | °C | |
| Oxygen Index | 36 | -- | % | ISO 4589-2 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SUPREME HIPS SH 810HF | Supreme Petrochem Ltd. | PS (HIPS) | SUPREME HIPS |
| Westlake LDPE EF378 | Westlake Chemical Corporation | LDPE | Westlake LDPE |
| UBESTA 3020 CX1 | UBE Engineering Plastics, S.A. | Nylon 12 | UBESTA |
| Estane® ETE 55DS3 TPU | Lubrizol Advanced Materials, Inc. | TPU-Polyester | Estane® |
| LAMIGAMID® 1200 | Schwartz Technical Plastic | Nylon 12 | LAMIGAMID® |