Sumikon® FM-MK115S
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | Sumitomo Bakelite Co., Ltd. |
| Trademark: | Sumikon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | CyuhZR_Sumikon-FM-MK115S.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PPS molding compounds developed for the purpose of metal substituion. They currently are extensively used in precision molded parts such as optical parts. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 2.12 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.20 | % | ASTM D955 |
| Transverse flow | 0.30 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.030 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 60.0 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 0.50 | % | ASTM D638 |
| Flexural Modulus | 21600 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 130 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 60 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 260 | °C | ASTM D648 |
| Thermal Conductivity | 0.90 | W/m/K | ASTM C177 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength | 15 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 5.00 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 6.0E-3 | ASTM D150 | |
| Arc Resistance | 190 | sec | ASTM D495 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 3.0 | hr | |
| Mold Temperature | 120 - 150 | °C |
| Injection instructions |
|---|
| Cylinder temperature: 290 to 340°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Razamid® A121 | Razin™ Engineering Plastics | Nylon 66 | Razamid® |
| Badaprene® TPV 60A 1065 | Bada AG | PP+EPDM | Badaprene® |
| ALTECH® PA6 A 2050/100 GF50 | ALBIS PLASTIC GmbH | Nylon 6 | ALTECH® PA6 |
| Leona™ 91G40 | Asahi Kasei Chemicals Corporation | Nylon 66 | Leona™ |
| Hostacom X M3 T14 C12507 | LyondellBasell Industries | PP Copolymer | Hostacom |