INSPIRE™ TF1311 SC
| Category: | TPO , Performance Polymers |
| Manufacturer: | Trinseo |
| Trademark: | INSPIRE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Cxs0gK_INSPIRE-TF1311-SC.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
INSPIRE* TF1311 SC is a natural 16% talc filled high impact PP. It has been developed for self-coloring (SC) in combination with the PP CCUVE 4% combi-masterbatches. This material combination, called INSPIRE* TF1311 ESU, is suitable for highly demanding aesthetic automotive applications, with superior scratch resistance and UV light stabilization. Applications:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.02 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 9.5 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.90 - 1.2 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1950 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 20.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 70 | % | ISO 527-2/50 |
| Flexural Modulus | 1850 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ISO 180/1A | ||
| 0°C | 8.0 | kJ/m² | ISO 180/1A |
| 23°C | 15 | kJ/m² | ISO 180/1A |
| Multi-Axial Instrumented Impact Energy (23°C, Energy to Break, Toughness Failure) | 70.0 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 110 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 58.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 135 | °C | ISO 306/A120 |
| CLTE - Flow | 8.5E-5 | cm/cm/°C | ASTM D696 |
| Additional Information |
|---|
| The information and data contained herein is specific to the natural (neat) product. For properties of the material in combination with PROMATCH* combi-masterbatches please refer to the technical data sheet for INSPIRE* TF1311 ESU. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Vipel® F764-BTX-00 | AOC, L.L.C. | Polyester Alloy | Vipel® |
| Unichem 9034 | Colorite Polymers | PVC, Unspecified | Unichem |
| Addisil™ 450 E | Momentive Performance Materials Inc. | Rubber | Addisil™ |
| BioCeres® BC-LBI02 | FuturaMat | Biodeg Polymers | BioCeres® |
| Axiall PVC 10805 | Axiall Corporation | PVC, Flexible | Axiall PVC |