AKROLOY® PA GF 50 natural (2916)
| Category: | Nylon 66+Nylon 6I/6T , Polyamide 66 + PA 6I/6T |
| Manufacturer: | AKRO-PLASTIC GmbH |
| Trademark: | AKROLOY® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | CxVymV_AKROLOY-PA-GF-50-natural-2916-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AKROLOY® PA GF 50 natural (2916) is a 50% glass fibre reinforced polyamide blend with very high stiffness and strength, even in conditioned state. Applications are components with high dimensional stability, independent from moisture content. AKROLOY® PA GF 50 is an alternative for aluminium- and zinc diecast alloys. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.59 | -- | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (275°C/5.0 kg) | 9.00 | -- | cm³/10min | ISO 1133 |
| Spiral Flow | 54.0 | -- | cm | Internal Method |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 0.50 | -- | % | |
| Flow | < 0.30 | -- | % | |
| Water Absorption (Saturation, 23°C) | 3.5 to 4.0 | -- | % | ISO 62 |
| Humidity Absorption - 62% RH (70°C) | 1.1 | -- | % | ISO 1110 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Temperature Index | IEC 216 | |||
| 50% Loss of Tensile Strength, 20000 hr | 110 to 130 | -- | °C | |
| 50% Loss of Tensile Strength, 5000 hr | 140 to 150 | -- | °C |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Ball Indentation Hardness (H 961/30) | 290 | -- | MPa | ISO 2039-1 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 17500 | 16500 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 250 | 220 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 3.0 | 3.0 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 16400 | -- | MPa | ISO 178 |
| Flexural Stress 2 | 380 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 15 | -- | kJ/m² | |
| 23°C | 17 | 17 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 95 | -- | kJ/m² | |
| 23°C | 110 | 100 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 245 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 225 | -- | °C | ISO 75-2/A |
| Vicat Softening Temperature | 242 | -- | °C | ISO 306/B50 |
| Melting Temperature 3 | 255 | -- | °C | DIN EN 11357-1 |
| CLTE | ISO 11359-2 | |||
| Flow : 23 to 80°C | 1.5E-5 | -- | cm/cm/°C | |
| Transverse : 23 to 80°C | 6.5E-5 | -- | cm/cm/°C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.5E+17 | -- | ohms | IEC 60093 |
| Volume Resistivity | 9.1E+13 | -- | ohms·cm | IEC 60093 |
| Relative Permittivity (1 MHz) | 4.42 | -- | IEC 60250 | |
| Comparative Tracking Index (Solution A) | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate 4(1.00 mm) | < 100 | -- | mm/min | FMVSS 302 |
| Flame Rating (0.800 mm) | HB | -- | UL 94 |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 10 K/min, DSC |
| 4 . | >1 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RJM TPS-G 30A | RJM International, Inc. | TPE | RJM |
| Titalon® 2500AGF | Titan Plastics Compounds Co., Ltd. | Nylon 66 | Titalon® |
| Ultramid® B3WG7 BK00564 | BASF Corporation | Nylon 6 | Ultramid® |
| Fiberfil® M-2501 BK | Fiberfil® Engineered Plastics Inc. | Nylon 66 | Fiberfil® |
| PMC® 746 | Smooth-On, Inc | PUR, Unspecified | PMC® |