Order Products : sales@su-jiao.com
Diakon® CTG825
| Category: | Acrylic (PMMA) , Polymethyl Methacrylate Acrylic |
| Manufacturer: | Lucite International Holland BV |
| Trademark: | Diakon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Cx8xMM_DiakonCTG825.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Diakon®CTG825 is a polymethyl methacrylate-acrylic material,. This product is available in Europe, and the processing method is injection molding. Diakon®The main characteristics of CTG825 are: flame retardant/rated flame. |
| General Information | |
|---|---|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.15 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/3.8 kg) | 2.3 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.40 - 0.80 | % | |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.35 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 55 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | 52.0 | MPa | ISO 527-2 |
| Flexural Modulus | 2300 | MPa | ISO 178 |
| Flexural Stress | 75.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 4.8 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | 54 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact | 4.8 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 95.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 110 | °C | ISO 306/A |
| -- | 95.0 | °C | ISO 306/B |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 | |
| Glow Wire Ignition Temperature | 650 | °C | IEC 60695-2-13 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Refractive Index | 1.490 | ISO 489 | |
| Transmittance | 92.0 | % | ASTM D1003 |
| Haze | 1.5 | % | ASTM D1003 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Hopper Temperature | 50 - 90 | °C | |
| Rear Temperature | 190 - 250 | °C | |
| Middle Temperature | 210 - 270 | °C | |
| Front Temperature | 210 - 290 | °C | |
| Nozzle Temperature | 220 - 280 | °C | |
| Mold Temperature | 50 - 90 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RapidVac™ VA-286 | Innovative Polymers, Inc. | TSU | RapidVac™ |
| Tritan™ MX731 | Eastman Chemical Company | Copolyester | Tritan™ |
| Axiall PVC 8676 | Axiall Corporation | PVC, Flexible | Axiall PVC |
| Karina BLACK PVC COMPOUND 809D48/ 1-C-IS-AS-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Lupoy® GN1006FM | LG Chem Ltd. | PC | Lupoy® |