ASTALAC™ ABS M112P
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Marplex Australia Pty. Ltd. |
| Trademark: | ASTALAC™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Cx4yyV_ASTALAC-ABS-M112P.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ASTALAC™ ABS M112P is an ultra high heat resistance grade of ABS designed to enhance the surface adhesion of docorated automotive interior components. The grade features an exacting balance of heat resistance, impact toughness, product rigidity and mouldability with typical applications in the automotive area including console capping mouldings and instrument panel fascias. Note: The letters "UV" or "W" indicate UV stabilisation has been added [ ie: ASTALAC™ ABS M112PUV ]. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.06 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 220°C/10.0 kg | 5.0 | g/10 min | |
| 230°C/3.8 kg | 2.0 | g/10 min | |
| Molding Shrinkage - Flow (3.00 mm) | 0.60 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.25 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 108 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(3.20 mm) | 52.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | 45 | % | ASTM D638 |
| Flexural Modulus 3(3.20 mm) | 2450 | MPa | ASTM D790 |
| Flexural Strength 4(3.20 mm) | 75.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 150 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 1.8 MPa, Unannealed, 3.20 mm | 90.0 | °C | |
| 1.8 MPa, Unannealed, 6.40 mm | 96.0 | °C | |
| 1.8 MPa, Unannealed, 12.7 mm | 105 | °C | |
| Vicat Softening Temperature | 118 | °C | ASTM D1525 5 |
| CLTE - Flow | 6.5E-5 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 | |
| Glow Wire Ignition Temperature (1.60 mm) | 550 | °C | AS/NZS 60695.2.12 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 to 95.0 | °C | |
| Drying Time | 3.0 to 6.0 | hr | |
| Rear Temperature | 215 to 235 | °C | |
| Middle Temperature | 225 to 245 | °C | |
| Front Temperature | 235 to 255 | °C | |
| Processing (Melt) Temp | 230 to 260 | °C | |
| Mold Temperature | 40.0 to 80.0 | °C | |
| Injection Pressure | 60.0 to 140 | MPa | |
| Injection Rate | Moderate | ||
| Back Pressure | 0.100 to 0.500 | MPa | |
| Screw Speed | 40 to 60 | rpm | |
| Clamp Tonnage | 3.0 to 6.0 | kN/cm² |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sinvicomp SRF9702/C | Teknor Apex Asia Pacific PTE. LTD. | PVC, Rigid | Sinvicomp |
| 4PROP® 25D11120 | 4Plas | PP Homopolymer | 4PROP® |
| Axiall PVC 8780 | Axiall Corporation | PVC, Flexible | Axiall PVC |
| Clariant ABS ABS6200 | Clariant Corporation | ABS | Clariant ABS |
| Grilon® BGM-30 X | EMS-GRIVORY | Nylon 6 | Grilon® |