SABIC® PP 48M10
| Category: | PP Impact Copolymer , Polypropylene Impact Copolymer |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | CwUcaP_SABIC-PP-48M10.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This grade has very good flow characteristics, high stiffness and good impact strength. It is suitable for articles with complex shapes, such as crates and boxes, rigid packaging and components for the automotive and electro-technical industries. This grade is also available with a combined processing and antistatic additive package. The product mentioned herein is in particular not tested and therefore not validated for use in pharmaceutical/medical applications. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| UL File Number |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.905 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 15 | g/10 min | ASTM D1238, ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 95 | ASTM D785 | |
| Shore Hardness (Shore D) | 65 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 1% Secant 1 | 1500 | MPa | ASTM D638 |
| -- | 1400 | MPa | ISO 527-2/1A/1 |
| Tensile Strength | |||
| Yield 2 | 26.0 | MPa | ASTM D638 |
| Yield | 26.0 | MPa | ISO 527-2/1A/50 |
| Tensile Elongation | |||
| Yield 3 | 5.0 | % | ASTM D638 |
| Yield | 5.0 | % | ISO 527-2/1A/50 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20°C | 6.0 | kJ/m² | |
| 0°C | 7.0 | kJ/m² | |
| 23°C | 11 | kJ/m² | |
| Notched Izod Impact | |||
| -20°C | 65 | J/m | ASTM D256A |
| 0°C | 75 | J/m | ASTM D256A |
| 23°C | 90 | J/m | ASTM D256A |
| -20°C | 5.0 | kJ/m² | ISO 180/1A |
| 0°C | 7.0 | kJ/m² | ISO 180/1A |
| 23°C | 8.0 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 95.0 | °C | ASTM D648 |
| 0.45 MPa, Unannealed 4 | 90.0 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed | 60.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed 5 | 55.0 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 151 | °C | ASTM D1525, ISO 306/A120 6 6 |
| -- | 79.0 | °C | ASTM D1525, ISO 306/B120 7 7 |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | testbar 80*10*4mm |
| 5 . | testbar 80*10*4mm |
| 6 . | Rate B (120°C/h), Loading 1 (10 N) |
| 7 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 899 X 120422 A | RTP Company | Acetal (POM) Copolymer | RTP |
| Sinvicomp SZF6208 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Flexible | Sinvicomp |
| ASTALON™ S3000RG | Marplex Australia Pty. Ltd. | PC | ASTALON™ |
| Clariant Nylon 6/6 PA-113GF30 TF15 | Clariant Corporation | Nylon 66 | Clariant Nylon 6/6 |
| Sylvin 9600-100UV Clear | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |