TYRIL™ 790
| Category: | SAN , SAN Resin |
| Manufacturer: | Trinseo |
| Trademark: | TYRIL™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | CuxN0b_TYRIL-790.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
TYRIL* styrene-acrylonitrile (SAN) resins are designed to offer superior chemical resistance, strength, hardness and dimensional stability in a broad range of product applications. The key property of TYRIL 790 is its high flow that results in excellent processabiltiy. TYRIL 790 is specifically designed for end-use applications requiring a good balance of physical properties, optical properties (gloss, clarity or opaqueness), heat resistance and practical toughness. Applications:
Complies with:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.08 | g/cm³ | ASTM D792, ISO 1183/B |
| -- | 1080 | kg/m³ | ISO 1183 1 |
| Apparent Density | 0.69 | g/cm³ | ASTM D1895, ISO 60 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238, ISO 1133 | ||
| 220°C/10.0 kg | 21 | g/10 min | |
| 230°C/3.8 kg | 9.0 | g/10 min | |
| Melt volume-flow rate (220°C/10.0 kg) | 28.0 | cm³/10min | ISO 1133 2 |
| Water Absorption | ISO 62 3 | ||
| Saturation | 0.10 | % | |
| Equilibrium | 0.60 | % | |
| Viscosity number | 91.0 | cm³/g | ISO 307, 1157, 1628 4 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 84 | ASTM D785, ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3800 | MPa | ASTM D638, ISO 527-2 |
| Tensile Stress | |||
| Yield | 76.0 | MPa | ISO 527-2 5 |
| Break 6 | 72.0 | MPa | ASTM D638 |
| Break | 72.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Yield) | 2.6 | % | ISO 527-2 7 |
| Nominal strain at break | 2.6 | % | ISO 527-2 8 |
| Flexural Strength | 98.0 | MPa | ASTM D790, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength | |||
| 23°C | 16 | kJ/m² | ISO 179 |
| -30°C | 18.0 | kJ/m² | ISO 179/1eU 9 |
| 23°C | 17.0 | kJ/m² | ISO 179/1eU 10 |
| Unnotched Izod Impact Strength (23°C) | 13 | kJ/m² | ISO 180 |
| Tensile notched impact strength (23°C) | 17.0 | kJ/m² | ISO 8256/1 11 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Annealed | 101 | °C | ASTM D648, ISO 75-2/A |
| 1.8 MPa | 101 | °C | ISO 75-2 12 |
| Vicat Softening Temperature | |||
| -- | 101 | °C | ASTM D1525, ISO 306/B50 5 13 |
| -- | 110 | °C | ASTM D1525, ISO 306/A120 6 14 |
| 50°C/h, B (50N) | 101 | °C | ISO 306 15 |
| CLTE | |||
| Flow | 5.0E-5 | cm/cm/°C | DIN 53752, ISO 11359-2 16 |
| Transverse | 6.0E-5 | cm/cm/°C | ISO 11359-2 17 |
| Specific Heat | 1380 | J/kg/°C | ASTM D2766 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface resistivity | > 1.0E+15 | ohms | IEC 60093 18 |
| Volume resistivity | > 1.0E+13 | ohms·m | IEC 60093 19 |
| Electric Strength | 9.1 | kV/mm | IEC 60243-1 |
| Relative Permittivity | |||
| 1 MHz | 2.80 | IEC 60250 | |
| 100 Hz | 3.00 | IEC 60250 20 | |
| Dissipation Factor | |||
| 1 MHz | 1.0E-4 | IEC 60250 | |
| 100 Hz | 8.0E-5 | IEC 60250 21 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating 22(1.60 mm) | HB | UL 94 | |
| Burning Behav. at 1.6mm nom. thickn. (1.50 mm, UL) | HB | ISO 1210 23 |
| Note Message | |
|---|---|
| 1 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 2 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 3 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 4 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 5 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 6 . | 5.0 mm/min |
| 7 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 8 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 9 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 10 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 11 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 12 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 13 . | Rate A (50°C/h), Loading 2 (50 N) |
| 14 . | Rate B (120°C/h), Loading 1 (10 N) |
| 15 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 16 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 17 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 18 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 19 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 20 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 21 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 22 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 23 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ateva® 1609 | Celanese EVA Performance Polymers | EVA | Ateva® |
| EVICOM™ WE 9075 | INEOS Compounds | PVC, Flexible | EVICOM™ |
| LightSpan® LS-6140 | NuSil Technology | Silicone | LightSpan® |
| SCHULAMID® 612 GF 33 HE | A. Schulman Europe | Nylon 612 | SCHULAMID® |
| Panlite® K-1285ZH | TEIJIN LIMITED | PC | Panlite® |