Lupox® GP1000SB
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | Lupox® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Cus05D_Lupox-GP1000SB.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Description Anti-Hydrolysis Applications IT/OA, Automotive (Connector) |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.30 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (235°C/2.16 kg) | 19 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 1.2 to 2.0 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.080 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, 3.20 mm) | 50.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | > 100 | % | ASTM D638 |
| Flexural Modulus 3(3.20 mm) | 2160 | MPa | ASTM D790 |
| Flexural Strength 4(Yield, 3.20 mm) | 72.6 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm) | 55 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.40 mm) | 57.0 | °C | ASTM D648 |
| Peak Melting Temperature | 223 | °C | ASTM D3418 |
| RTI Elec | 140 | °C | UL 746 |
| RTI Imp | 130 | °C | UL 746 |
| RTI Str | 140 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+17 | ohms·cm | ASTM D257 |
| Dielectric Strength (1.00 mm) | 23 | kV/mm | ASTM D149 |
| Arc Resistance | PLC 5 | ASTM D495 | |
| Comparative Tracking Index (CTI) 5 | PLC 0 | UL 746 | |
| Comparative Tracking Index (Solution A) | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.710 mm | HB | ||
| 1.50 mm | HB | ||
| 3.30 mm | HB |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 to 120 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 230 to 235 | °C | |
| Middle Temperature | 235 to 240 | °C | |
| Front Temperature | 240 to 245 | °C | |
| Nozzle Temperature | 240 to 250 | °C | |
| Processing (Melt) Temp | 240 to 250 | °C | |
| Mold Temperature | 40.0 to 80.0 | °C |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 2.8 mm/min |
| 4 . | 2.8 mm/min |
| 5 . | Solution A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Purell HP671T | LyondellBasell Industries | PP Homopolymer | Purell |
| RheTech Thermoplastic Polyolefin FT3080-757UV | RheTech, Inc. | Polyolefin, Unspecified | RheTech Thermoplastic Polyolefin |
| ADDINYL A2 ZV15 | ADDIPLAST | Nylon 66 | ADDINYL |
| Generic TPO - Glass Fiber | Generic | TPO | Generic |
| LEXAN™ HP2R resin | SABIC Innovative Plastics Europe | PC | LEXAN™ |