Toyolac® 100G-10
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Toray Resin Company |
| Trademark: | Toyolac® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | CumRc5_Toyolac-100G-10.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Toyolac® 100G-10 is an Acrylonitrile Butadiene Styrene (ABS) product filled with 10% glass fiber. It is available in Asia Pacific, Europe, or North America. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Part Marking Code |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.11 | g/cm³ | ASTM D792 |
| 23°C | 1.11 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (240°C/10.0 kg) | 24 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.20 to 0.40 | % | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale, 23°C) | 118 | ASTM D785, ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| -- | 78.0 | MPa | ASTM D638 |
| 23°C | 81.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Break | 3.0 | % | ASTM D638 |
| Break, 23°C | 3.0 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 4100 | MPa | ASTM D790 |
| 23°C | 4200 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 120 | MPa | ASTM D790 |
| 23°C | 127 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 9.0 | kJ/m² | ISO 179 |
| Notched Izod Impact (23°C, 12.7 mm) | 83 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 6.40 mm | 100 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 100 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 95.0 | °C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC X3676 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| Dialon 1015GF20V0 | DTR S.r.l. (Develop Thermoplastic Resins) | PC | Dialon |
| Kaneka MUH E7301 | Kaneka Corporation | ABS | Kaneka MUH |
| OnForce™ LFT LF5200-5017 Grey | PolyOne Corporation | Polyolefin, Unspecified | OnForce™ LFT |
| LNP™ LUBRICOMP™ KFL36 compound | SABIC Innovative Plastics | Acetal (POM) Copolymer | LNP™ LUBRICOMP™ |